- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.94
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.214
- 拉伸强度 [MPa]: 15.0
- 断裂伸长率 [%]: 31.0
- 弯曲强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 0.239
- 硬度: 40.0
- 热变形温度 [℃]: 72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 - 1.52 g/cc | 0.0340 - 0.0549 lb/in³ | Average value: 1.15 g/cc Grade Count:115 |
| Filler Content | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 26.2 % Grade Count:26 |
| Water Absorption | 0.0100 - 0.300 % | 0.0100 - 0.300 % | Average value: 0.0579 % Grade Count:28 |
| Linear Mold Shrinkage | 0.00100 - 0.0150 cm/cm | 0.00100 - 0.0150 in/in | Average value: 0.00474 cm/cm Grade Count:103 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00400 - 0.00700 cm/cm | 0.00400 - 0.00700 in/in | Average value: 0.00529 cm/cm Grade Count:14 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.00900 cm/cm | 0.00500 - 0.00900 in/in | Average value: 0.00770 cm/cm Grade Count:5 |
| Melt Flow | 1.00 - 74.2 g/10 min | 1.00 - 74.2 g/10 min | Average value: 9.94 g/10 min Grade Count:81 |
| Spiral Flow | 95.0 - 106 cm @Temperature 250 - 250 °C | 37.4 - 41.7 in @Temperature 482 - 482 °F | Average value: 101 cm Grade Count:2 |
| 95.0 - 106 cm @Thickness 2.00 - 2.00 mm | 37.4 - 41.7 in @Thickness 0.0787 - 0.0787 in | Average value: 101 cm Grade Count:2 | |
| Ash | 30.0 - 35.0 % | 30.0 - 35.0 % | Average value: 30.2 % Grade Count:26 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 53.0 - 70.0 | 53.0 - 70.0 | Average value: 64.0 Grade Count:3 |
| Hardness, Rockwell R | 40.0 - 117 | 40.0 - 117 | Average value: 88.3 Grade Count:52 |
| Hardness, Shore D | 73.0 - 79.0 | 73.0 - 79.0 | Average value: 75.4 Grade Count:14 |
| Ball Indentation Hardness | 28.0 - 66.0 MPa | 4060 - 9570 psi | Average value: 48.9 MPa Grade Count:7 |
| Tensile Strength, Ultimate | 20.0 - 150 MPa | 2900 - 21800 psi | Average value: 50.1 MPa Grade Count:81 |
| 9.00 - 45.0 MPa @Temperature 60.0 - 120 °C | 1310 - 6530 psi @Temperature 140 - 248 °F | Average value: 22.3 MPa Grade Count:2 | |
| Tensile Strength, Yield | 15.0 - 115 MPa | 2180 - 16700 psi | Average value: 45.1 MPa Grade Count:56 |
| 48.0 - 48.0 MPa @Temperature 100 - 100 °C | 6960 - 6960 psi @Temperature 212 - 212 °F | Average value: 48.0 MPa Grade Count:1 | |
| Elongation at Break | 1.00 - 37.0 % | 1.00 - 37.0 % | Average value: 6.09 % Grade Count:68 |
| 5.50 - 7.50 % @Temperature 100 - 100 °C | 5.50 - 7.50 % @Temperature 212 - 212 °F | Average value: 6.50 % Grade Count:2 | |
| Elongation at Yield | 3.00 - 100 % | 3.00 - 100 % | Average value: 7.60 % Grade Count:42 |
| Modulus of Elasticity | 1.85 - 12.3 GPa | 268 - 1780 ksi | Average value: 4.81 GPa Grade Count:49 |
| 3.50 - 4.50 GPa @Temperature 100 - 100 °C | 508 - 653 ksi @Temperature 212 - 212 °F | Average value: 4.00 GPa Grade Count:2 | |
| Flexural Yield Strength | 31.0 - 160 MPa | 4500 - 23200 psi | Average value: 78.7 MPa Grade Count:73 |
| Flexural Modulus | 0.239 - 8.40 GPa | 34.7 - 1220 ksi | Average value: 4.20 GPa Grade Count:113 |
| 0.600 - 2.10 GPa @Temperature 60.0 - 120 °C | 87.0 - 305 ksi @Temperature 140 - 248 °F | Average value: 1.47 GPa Grade Count:1 | |
| Compressive Yield Strength | 39.3 - 62.1 MPa | 5700 - 9000 psi | Average value: 50.7 MPa Grade Count:7 |
| Izod Impact, Notched | 0.214 - 6.00 J/cm | 0.400 - 11.2 ft-lb/in | Average value: 0.716 J/cm Grade Count:96 |
| 0.250 - 2.00 J/cm @Temperature -40.0 - 0.000 °C | 0.468 - 3.75 ft-lb/in @Temperature -40.0 - 32.0 °F | Average value: 1.09 J/cm Grade Count:3 | |
| 2.1356 - 2.1356 J/cm @Temperature -28.9 - -28.9 °C | 4.0009 - 4.0009 ft-lb/in @Temperature -20.0 - -20.0 °F | Average value: 1.09 J/cm Grade Count:1 | |
| 2.1356 - 2.1356 J/cm @Thickness 3.17 - 3.17 mm | 4.0009 - 4.0009 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.09 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 1.60 - 7.47 J/cm | 3.00 - 14.0 ft-lb/in | Average value: 3.76 J/cm Grade Count:34 |
| 1.0678 - 1.0678 J/cm @Temperature -18.0 - -18.0 °C | 2.0004 - 2.0004 ft-lb/in @Temperature -0.400 - -0.400 °F | Average value: 1.07 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 5.10 - 33.0 kJ/m² | 2.43 - 15.7 ft-lb/in² | Average value: 16.2 kJ/m² Grade Count:7 |
| 3.70 - 5.00 kJ/m² @Temperature -40.0 - 0.000 °C | 1.76 - 2.38 ft-lb/in² @Temperature -40.0 - 32.0 °F | Average value: 4.37 kJ/m² Grade Count:7 | |
| Charpy Impact Unnotched | 1.20 J/cm² - NB | 5.71 ft-lb/in² - NB | Average value: 6.02 J/cm² Grade Count:14 |
| 1.00 J/cm² - NB @Temperature -40.0 - -20.0 °C | 4.76 ft-lb/in² - NB @Temperature -40.0 - -4.00 °F | Average value: 4.54 J/cm² Grade Count:14 | |
| Charpy Impact, Notched | 0.690 - 3.70 J/cm² | 3.28 - 17.6 ft-lb/in² | Average value: 1.95 J/cm² Grade Count:15 |
| 0.250 - 3.20 J/cm² @Temperature -30.0 - -20.0 °C | 1.19 - 15.2 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 0.829 J/cm² Grade Count:12 | |
| Gardner Impact | 0.339 - 4.52 J | 0.250 - 3.33 ft-lb | Average value: 0.693 J Grade Count:22 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+17 ohm-cm | 1.00e+15 - 1.00e+17 ohm-cm | Average value: 2.97e+16 ohm-cm Grade Count:16 |
| Dielectric Constant | 2.50 - 3.50 | 2.50 - 3.50 | Average value: 2.94 Grade Count:11 |
| Dielectric Strength | 19.7 - 30.0 kV/mm | 500 - 762 kV/in | Average value: 22.5 kV/mm Grade Count:15 |
| Dissipation Factor | 0.00200 - 0.00600 | 0.00200 - 0.00600 | Average value: 0.00286 Grade Count:7 |
| Arc Resistance | 120 - 130 sec | 120 - 130 sec | Average value: 125 sec Grade Count:11 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 21.6 - 75.0 µm/m-°C | 12.0 - 41.7 µin/in-°F | Average value: 41.9 µm/m-°C Grade Count:15 |
| Thermal Conductivity | 0.303 - 0.360 W/m-K | 2.10 - 2.50 BTU-in/hr-ft²-°F | Average value: 0.336 W/m-K Grade Count:9 |
| Melting Point | 163 - 182 °C | 325 - 360 °F | Average value: 171 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 - 169 °C | 162 - 336 °F | Average value: 147 °C Grade Count:104 |
| Deflection Temperature at 1.8 MPa (264 psi) | 35.6 - 162 °C | 96.0 - 324 °F | Average value: 118 °C Grade Count:103 |
| Vicat Softening Point | 43.0 - 160 °C | 109 - 320 °F | Average value: 108 °C Grade Count:17 |
| Flammability, UL94 | HB | HB | Grade Count:31 |
| Flammability Test | 1.20 - 125 | 1.20 - 125 | Average value: 83.7 Grade Count:3 |
| Oxygen Index | 21.0 % | 21.0 % | Average value: 21.0 % Grade Count:3 |
| Glow Wire Test | 650 - 750 °C | 1200 - 1380 °F | Average value: 683 °C Grade Count:3 |
| Shrinkage | 0.100 - 1.70 % | 0.100 - 1.70 % | Average value: 0.755 % Grade Count:6 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 30.0 - 260 °C | 86.0 - 500 °F | Average value: 209 °C Grade Count:23 |
| Nozzle Temperature | 54.4 - 243 °C | 130 - 470 °F | Average value: 220 °C Grade Count:27 |
| Melt Temperature | 190 - 270 °C | 374 - 518 °F | Average value: 227 °C Grade Count:48 |
| Mold Temperature | 26.7 - 100 °C | 80.0 - 212 °F | Average value: 47.1 °C Grade Count:61 |
| Drying Temperature | 65.6 - 100 °C | 150 - 212 °F | Average value: 77.8 °C Grade Count:33 |
| Dry Time | 1.00 - 4.00 hour | 1.00 - 4.00 hour | Average value: 2.15 hour Grade Count:30 |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.0600 % Grade Count:15 |
| Injection Pressure | 2.76 - 120 MPa | 400 - 17400 psi | Average value: 51.1 MPa Grade Count:34 |
| Hold Pressure | 2.07 - 80.0 MPa | 300 - 11600 psi | Average value: 8.83 MPa Grade Count:15 |
| Back Pressure | 0.000 - 3.92 MPa | 0.000 - 569 psi | Average value: 0.986 MPa Grade Count:19 |
| Screw Speed | 20.0 - 150 rpm | 20.0 - 150 rpm | Average value: 56.3 rpm Grade Count:6 |