- 密度 [g/cm3]: 1.57
- 吸水率 [%]: 0.217
- 缺口冲击强度: 0.184
- 弯曲强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.680 g/cc | 0.0246 lb/in³ | ASTM D1895 |
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Water Absorption | 0.217 % | 0.217 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00227 cm/cm | 0.00227 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 79 | 79 | ASTM D785 |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 0.45 % | 0.45 % | ASTM D638 |
| Tensile Modulus | 11.1 GPa | 1610 ksi | ASTM D638 |
| Flexural Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Compressive Strength | 164 MPa | 23800 psi | ASTM D695 |
| Izod Impact, Notched | 0.184 J/cm | 0.345 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.206 J/cm² | 0.980 ft-lb/in² | ASTM D256 |
| Impact | 115 | 115 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.4 | 4.4 | ASTM D150 |
| Dielectric Strength | 13.6 kV/mm | 345 kV/in | Step by Step; ASTM D149 |
| 16.3 kV/mm | 414 kV/in | Short Time; ASTM D149 | |
| Dielectric Breakdown | 18000 V | 18000 V | 1hr 82C; ASTM D149 |
| Dissipation Factor | 0.036 | 0.036 | ASTM D150 |
| Arc Resistance | 184 sec | 184 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.620 W/m-K @Temperature 100 °C | 4.30 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 211 °C | 412 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Shrinkage | 0.075 % | 0.075 % | 72 hr, 120ºC; ASTM D1299 |