- 密度 [g/cm3]: 1.85
- 吸水率 [%]: 0.03
- 断裂伸长率 [%]: 89.8
- 弯曲强度 [MPa]: 46.0
- 弯曲模量 [MPa]: 14.36
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.890 g/cc | 0.0322 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.030 % | 0.030 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0039 cm/cm | 0.0039 in/in | per ATM D955. Post shrinkage is 0.07% at 72hr 120ºC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 74 | 74 | ASTM D785 |
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 0.47 % | 0.47 % | ASTM D638 |
| Tensile Modulus | 12.98 GPa | 1883 ksi | ASTM D638 |
| Flexural Yield Strength | 89.8 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 14.36 GPa | 2083 ksi | ASTM D790 |
| Compressive Yield Strength | 174.2 MPa | 25270 psi | ASTM D695 |
| Poissons Ratio | 0.27 | 0.27 | In tension |
| Shear Modulus | 5.12 GPa | 743 ksi | Calculated |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ASTM D256 |
| Impact | 71 | 71 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.646e+12 ohm-cm | 3.646e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.9 @Frequency 1e+6 Hz | 4.9 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.041 @Frequency 1e+6 Hz | 0.041 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 37.0 µm/m-°C @Temperature 20.0 °C | 20.6 µin/in-°F @Temperature 68.0 °F | |
| Maximum Service Temperature, Air | 202 °C | 396 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 164 °C | 327 °F | ASTM D648 |