- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.41
- 缺口冲击强度: 0.21
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 7.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.570 g/cc | 0.0206 lb/in³ | ASTM D1895 |
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.41 % | 0.41 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0066 cm/cm | 0.0066 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 0.76 % | 0.76 % | ASTM D638 |
| Tensile Modulus | 8.10 GPa | 1170 ksi | ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Strength | 209 MPa | 30300 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 3.00 GPa | 435 ksi | Calculated |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.199 J/cm² | 0.947 ft-lb/in² | ASTM D256 |
| Impact | 85 | 85 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.90e+11 ohm-cm | 4.90e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.6 | 4.6 | ASTM D150 |
| Dielectric Strength | 11.1 kV/mm | 282 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.048 | 0.048 | ASTM D150 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 193 °C | 379 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 25.8 % | 25.8 % | ASTM D2863 |
| Shrinkage | 0.26 % | 0.26 % | 72 hr, 120ºC; ASTM D1299 |