- 熔体流动速率 [g/10min]: 1.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.917 g/cc | 0.917 g/cc | ASTM D1505/D792 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 1000 % | 1000 % | ASTM D882 |
| Film Elongation at Break, TD | 1280 % | 1280 % | ASTM D882 |
| Elmendorf Tear Strength MD | 80 g | 80 g | gF; ASTM D1922 |
| Elmendorf Tear Strength TD | 560 g | 560 g | gF; ASTM D1922 |
| Dart drop Test | 100 g | 0.221 lb | gF/50%f; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| 1% Secant Modulus, MD | 180 MPa | 26100 psi | ASTM D882 |
| 1% Secant Modulus, TD | 210 MPa | 30500 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % @Thickness 0.0380 mm | 12 % @Thickness 0.00150 in | ASTM D1003 |
| Gloss | 98 % @Thickness 0.0380 mm | 98 % @Thickness 0.00150 in | 60°; ASTM D2457 |