- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.9215
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9215 g/cc | 0.03329 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Antiblock Level | 2500 ppm | 2500 ppm | |
| Slip Level | 1200 ppm | 1200 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.15 MPa | 1617 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.84 MPa | 1717 psi | ASTM D882 |
| Film Elongation at Break, MD | 393 % | 393 % | ASTM D882 |
| Film Elongation at Break, TD | 605 % | 605 % | ASTM D882 |
| Secant Modulus, MD | 0.203395 GPa | 29.5005 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.235801 GPa | 34.2005 ksi | 2% Secant; ASTM D882 |
| Impact | 89 | 89 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 870 | 870 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 984 | 984 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 266 g | 266 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 679 g | 679 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 13.09 g/micron | 332.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 33.415 g/micron | 848.75 g/mil | ASTM D1922 |
| Dart drop Test | 163 g | 0.359 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 39.08 MPa | 5668 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.54 MPa | 3704 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D1003 |
| Gloss | 48 % | 48 % | 45°; ASTM D2457 |