- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.9255
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9255 g/cc | 0.03344 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 13.89 MPa | 2015 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 14.58 MPa | 2115 psi | ASTM D882 |
| Film Elongation at Break, MD | 597 % | 597 % | ASTM D882 |
| Film Elongation at Break, TD | 660 % | 660 % | ASTM D882 |
| Secant Modulus, MD | 0.276873 GPa | 40.1576 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.330348 GPa | 47.9137 ksi | 2% Secant; ASTM D882 |
| Impact | 21.8 | 21.8 | [lbf]; Puncture Resistance Force; Dow Method |
| Puncture Energy | 6.91 J | 5.10 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 564 g | 564 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1110 g | 1110 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 11.1 g/micron | 282 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 21.9 g/micron | 555 g/mil | ASTM D1922 |
| Dart drop Test | 409 g | 0.902 lb | Method B; ASTM D1709 |
| Film Tensile Strength at Break, MD | 57.50 MPa | 8339 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 51.95 MPa | 7534 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 120 °C | 248 °F | 2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 111 °C | 232 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D1003 |
| Gloss | 60 % | 60 % | 45°; ASTM D2457 |