- 熔体流动速率 [g/10min]: 2.45
- 密度 [g/cm3]: 0.9178
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.9178 g/cc | 0.03316 lb/in³ | ASTM D792 | ||
| Thickness | 20.3 microns | 0.800 mil | |||
| Melt Flow | 2.45 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.45 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.22 MPa | 1628 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.5 MPa | 1530 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 519 % | 519 % | ASTM D882 | ||
| Film Elongation at Break, TD | 828 % | 828 % | ASTM D882 | ||
| Elongation at Break | 332 % | 332 % | on-pallet testing: Ultimate Stretch; Highlight Industries, Inc. Method | ||
| Secant Modulus, MD | 0.147437 GPa | 21.3843 ksi | 2% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.155711 GPa | 22.5844 ksi | 2% Secant; ASTM D882 | ||
| Impact | 9.0 | 9.0 | [lbf]; Puncture Resistance Force; Dow Method | ||
| 319 | 319 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |||
| 2524 | 2524 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |||
| 3246 | 3246 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |||
| Puncture Energy | 3.84 J | 2.83 ft-lb | Dow Method | ||
| Elmendorf Tear Strength MD | 184 g | 184 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength TD | 617 g | 617 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 9.06 g/micron | 230 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 30.364 g/micron | 771.25 g/mil | ASTM D1922 | ||
| Dart drop Test | <= 100 g | <= 0.221 lb | Method B; ASTM D1709 | ||
| 130 g | 0.287 lb | Method A; ASTM D1709 | |||
| Film Tensile Strength at Break, MD | 49.79 MPa | 7221 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 36.10 MPa | 5236 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) | ||
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.0 % | 1.0 % | ASTM D1003 | ||
| Gloss | 95 % | 95 % | 45°; ASTM D2457 | ||
| 156 % | 156 % | 20°; ASTM D2457 | |||
| Descriptive Properties | |||||
| Cling g | 214 | ASTM D5458, unstretched | |||