- 熔体流动速率 [g/10min]: 2.45
- 密度 [g/cm3]: 0.9178
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.9178 g/cc | 0.03316 lb/in³ | ASTM D792 | ||
| Thickness | 50.8 microns | 2.00 mil | |||
| Melt Flow | 2.45 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.45 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.21 MPa | 1481 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.984 MPa | 1448 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 723 % | 723 % | ASTM D882 | ||
| Film Elongation at Break, TD | 899 % | 899 % | ASTM D882 | ||
| Elongation at Break | 516 % | 516 % | on-pallet testing: Ultimate Stretch; Highlight Industries, Inc. Method | ||
| Secant Modulus, MD | 0.142046 GPa | 20.6023 ksi | 2% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.141591 GPa | 20.5363 ksi | 2% Secant; ASTM D882 | ||
| Impact | 19 | 19 | [lbf]; Puncture Resistance Force; Dow Method | ||
| 252 | 252 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |||
| 3077 | 3077 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |||
| 4039 | 4039 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |||
| Puncture Energy | 8.25 J | 6.08 ft-lb | Dow Method | ||
| Elmendorf Tear Strength MD | 781 g | 781 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength TD | 1145 g | 1145 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 15.37 g/micron | 390.5 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 22.54 g/micron | 572.5 g/mil | ASTM D1922 | ||
| Dart drop Test | 170 g | 0.375 lb | Method B; ASTM D1709 | ||
| 270 g | 0.595 lb | Method A; ASTM D1709 | |||
| Film Tensile Strength at Break, MD | 38.36 MPa | 5564 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 44.17 MPa | 6406 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) | ||
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.0 % | 4.0 % | ASTM D1003 | ||
| Gloss | 91 % | 91 % | 45°; ASTM D2457 | ||
| 146 % | 146 % | 20°; ASTM D2457 | |||
| Descriptive Properties | |||||
| Cling g | 276 | ASTM D5458, unstretched | |||