- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.932
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Antiblock Level | 3500 ppm | 3500 ppm | |
| Slip Level | 1200 ppm | 1200 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 16.77 MPa | 2433 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 17.5 MPa | 2540 psi | ASTM D882 |
| Film Elongation at Break, MD | 760 % | 760 % | ASTM D882 |
| Film Elongation at Break, TD | 806 % | 806 % | ASTM D882 |
| Secant Modulus, MD | 0.312443 GPa | 45.3167 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.312788 GPa | 45.3667 ksi | 2% Secant; ASTM D882 |
| Impact | 16 | 16 | [lbf]; Puncture Resistance Force; Dow Method |
| 103 | 103 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 4414 | 4414 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| 4427 | 4427 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| Puncture Energy | 3.62 J | 2.67 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 666 g | 666 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 1129 g | 1129 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 13.1 g/micron | 333 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.22 g/micron | 564.5 g/mil | ASTM D1922 |
| Dart drop Test | 106 g | 0.234 lb | Method A; ASTM D1709 |
| 112 g | 0.247 lb | Method B; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 58.82 MPa | 8531 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 52.23 MPa | 7576 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 23.5 N | 5.28 lb (f) | at 160°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 130 °C | 266 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Dow Method (DSC) |
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 17 % | 17 % | ASTM D1003 |
| Gloss | 41 % | 41 % | 20°; ASTM D2457 |
| 49 % | 49 % | 45°; ASTM D2457 | |