- 熔体流动速率 [g/10min]: 105.0
- 密度 [g/cm3]: 0.93
- 缺口冲击强度: 23.0
- 拉伸强度 [MPa]: 10.6
- 弯曲强度 [MPa]: 8.2
- 弯曲模量 [MPa]: 0.503
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.930 g/cc | 0.0336 lb/in³ | |
Viscosity | 21000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 21000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
29000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 29000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
31000 cP @Shear Rate 300 1/s, Temperature 190 °C | 31000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
Melt Flow | 105 g/10 min @Load 2.16 kg | 105 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 6.5. |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Ultimate | 8.20 MPa | 1190 psi | |
Tensile Strength, Yield | 10.6 MPa | 1540 psi | |
Elongation at Break | 450 % | 450 % | |
Modulus of Elasticity | 0.273 GPa | 39.6 ksi | Molded Sample 2% Secant Modulus |
Flexural Modulus | 0.503 GPa | 73.0 ksi | |
Izod Impact, Notched (ISO) | 23.0 kJ/m² @Temperature -50.0 °C | 10.9 ft-lb/in² @Temperature -58.0 °F | |
Thermal Properties | Metric | English | Comments |
Vicat Softening Point | 100 °C | 212 °F |