- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.929
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.929 g/cc | 0.0336 lb/in³ | ASTM D792 |
Thickness | 25.4 microns | 1.00 mil | |
Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ASTM D882 |
Film Tensile Strength at Yield, TD | 15.0 MPa | 2180 psi | ASTM D882 |
Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
Secant Modulus, MD | 0.275 GPa | 39.9 ksi | ASTM D882 |
Secant Modulus, TD | 0.330 GPa | 47.9 ksi | ASTM D882 |
Coefficient of Friction | <= 0.20 | <= 0.20 | ASTM D1894 |
Elmendorf Tear Strength, MD | 4.00 g/micron | 102 g/mil | ASTM D1922 |
Elmendorf Tear Strength, TD | 26.0 g/micron | 660 g/mil | ASTM D1922 |
Dart Drop | 4.40 g/micron | 112 g/mil | F50; ASTM D 1709/A |
Film Tensile Strength at Break, MD | 48.0 MPa | 6960 psi | ASTM D882 |
Film Tensile Strength at Break, TD | 36.0 MPa | 5220 psi | ASTM D882 |