- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg | 2.3 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.3. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | |
| Film Tensile Strength at Yield, TD | 8.30 MPa | 1200 psi | |
| Film Elongation at Break, MD | 550 % | 550 % | |
| Film Elongation at Break, TD | 750 % | 750 % | |
| Elmendorf Tear Strength MD | 330 g | 330 g | |
| Elmendorf Tear Strength TD | 540 g | 540 g | |
| Elmendorf Tear Strength, MD | 13.2 g/micron | 335 g/mil | |
| Elmendorf Tear Strength, TD | 21.6 g/micron | 549 g/mil | |
| Film Tensile Strength at Break, MD | 60.0 MPa | 8700 psi | |
| Film Tensile Strength at Break, TD | 34.0 MPa | 4930 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 0.80 % | 0.80 % | |
| Gloss | 92 % | 92 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 °C | 525 °F | Film extrusion temperature |