- 熔体流动速率 [g/10min]: 35.0
- 密度 [g/cm3]: 0.926
- 拉伸强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.250
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D4883 | ||
| Environmental Stress Crack Resistance | <= 1.0 hour | <= 1.0 hour | Condition B, 10%; ASTM D1693 | ||
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 190 °C | 35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 11.00 MPa | 1595 psi | ASTM D638 | ||
| Elongation at Break | 116 % | 116 % | ASTM D638 | ||
| Flexural Modulus | 0.250 GPa | 36.2 ksi | 1% secant; ASTM D790 | ||
| Tensile Impact Strength | 233 kJ/m² | 111 ft-lb/in² | at -40°C; ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | ASTM D3418 | ||
| Crystallization Temperature | 106 °C | 223 °F | ASTM D3418 | ||
| Vicat Softening Point | 92.2 °C | 198 °F | ASTM D1525 | ||
| Brittleness Temperature | >= -70.0 °C | >= -94.0 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Features | Standard processing antioxidants | ||||
| Form | PELLET | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.