- 熔体流动速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 6.0 % | 6.0 % | AT Plastics PTM-39 |
| Thickness | 31.0 microns | 1.22 mil | |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, MD | 440 % | 440 % | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, TD | 560 % | 560 % | Method A (500 mm/min); ASTM D882 |
| Secant Modulus, MD | 0.120 GPa | 17.4 ksi | 1% Secant Modulus; ASTM D882 |
| Secant Modulus, TD | 0.115 GPa | 16.7 ksi | 1% Secant Modulus; ASTM D882 |
| Dart Drop | 2.80 g/micron | 71.1 g/mil | f50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | Method A (500 mm/min); ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 °C | 219 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 68 % | 68 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 210 °C | 320 - 410 °F | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |