- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.927
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 6.0 % | 6.0 % | AT Plastics PTM-39 |
| Thickness | 60.0 microns | 2.36 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, MD | 360 % | 360 % | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | Method A (500 mm/min); ASTM D882 |
| Secant Modulus, MD | 0.120 GPa | 17.4 ksi | 1% Secant Modulus; ASTM D882 |
| Secant Modulus, TD | 0.130 GPa | 18.9 ksi | 1% Secant Modulus; ASTM D882 |
| Dart Drop | 2.80 g/micron | 71.1 g/mil | f50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | Method A (500 mm/min); ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 103 °C | 217 °F | DSC; ASTM D3417 |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | ASTM D1003 |
| Gloss | 45 % | 45 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |