- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.93
- 脆化温度 [℃]: -90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 6.0 % | 6.0 % | AT Plastics PTM-39 |
| Thickness | 130 microns | 5.12 mil | |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.00 MPa | 1160 psi | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, MD | 280 % | 280 % | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, TD | 530 % | 530 % | Method A (500 mm/min); ASTM D882 |
| Secant Modulus, MD | 0.125 GPa | 18.1 ksi | 1% Secant Modulus; ASTM D882 |
| Secant Modulus, TD | 0.140 GPa | 20.3 ksi | 1% Secant Modulus; ASTM D882 |
| Dart Drop | 5.60 g/micron | 142 g/mil | f50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | Method A (500 mm/min); ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 °C | 219 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Brittleness Temperature | -90.0 °C | -130 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 26 % | 26 % | ASTM D1003 |
| Gloss | 26 % | 26 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |