Overview of materials for Nylon 66, 30% Carbon Fiber Filled

Overview of materials for Nylon 66, 30% Carbon Fiber Filled 物性表: Overview of materials for Nylon 66, 30% Carbon Fiber Filled物性表及特性介绍,Overview of materials for Nylon 66, 30% Carbon Fiber Filled注塑参数详情,如需Overview of materials for Nylon 66, 30% Carbon Fiber Filled下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.21
  • 吸水率 [%]: 0.4
  • 缺口冲击强度: 0.534
  • 断裂伸长率 [%]: 215
  • 弯曲强度 [MPa]: 137.0
  • 弯曲模量 [MPa]: 0.0000193
  • 硬度: 97.0
  • 热变形温度 [℃]: 240.0
 
Physical PropertiesMetricEnglishComments
Density 1.21 - 1.57 g/cc0.0437 - 0.0567 lb/in³Average value: 1.30 g/cc Grade Count:27
Filler Content 25.0 - 30.0 %25.0 - 30.0 %Average value: 29.2 % Grade Count:13
Water Absorption 0.400 - 2.40 %0.400 - 2.40 %Average value: 0.751 % Grade Count:13
Moisture Absorption at Equilibrium 1.70 - 2.30 %1.70 - 2.30 %Average value: 1.92 % Grade Count:4
Viscosity Measurement 0.110 - 1450.110 - 145Average value: 96.8 Grade Count:3
Linear Mold Shrinkage 0.000200 - 0.0150 cm/cm0.000200 - 0.0150 in/inAverage value: 0.00263 cm/cm Grade Count:24
Linear Mold Shrinkage, 6.35 mm section 0.00200 cm/cm0.00200 in/inAverage value: 0.00200 cm/cm Grade Count:4
Linear Mold Shrinkage, Transverse 0.00400 - 0.0120 cm/cm0.00400 - 0.0120 in/inAverage value: 0.00726 cm/cm Grade Count:8
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 97.0 - 12097.0 - 120Average value: 116 Grade Count:7
Tensile Strength, Ultimate 137 - 300 MPa19900 - 43500 psiAverage value: 213 MPa Grade Count:25
 105 - 260 MPa
@Temperature -40.0 - 120 °C
15200 - 37700 psi
@Temperature -40.0 - 248 °F
Average value: 163 MPa Grade Count:2
Elongation at Break 1.00 - 4.00 %1.00 - 4.00 %Average value: 2.30 % Grade Count:24
Modulus of Elasticity 16.0 - 33.1 GPa2320 - 4800 ksiAverage value: 21.5 GPa Grade Count:20
Flexural Yield Strength 215 - 420 MPa31200 - 60900 psiAverage value: 316 MPa Grade Count:21
 140 - 337 MPa
@Temperature -40.0 - 80.0 °C
20300 - 48900 psi
@Temperature -40.0 - 176 °F
Average value: 252 MPa Grade Count:1
Flexural Modulus 0.0000193 - 29.0 GPa0.00280 - 4200 ksiAverage value: 15.9 GPa Grade Count:23
 7.20 - 19.0 GPa
@Temperature -40.0 - 120 °C
1040 - 2760 ksi
@Temperature -40.0 - 248 °F
Average value: 11.9 GPa Grade Count:2
Compressive Yield Strength 152 - 172 MPa22000 - 25000 psiAverage value: 164 MPa Grade Count:4
Izod Impact, Notched 0.534 - 2.40 J/cm1.00 - 4.50 ft-lb/inAverage value: 1.22 J/cm Grade Count:18
 0.550 - 0.800 J/cm
@Temperature -40.0 - -20.0 °C
1.03 - 1.50 ft-lb/in
@Temperature -40.0 - -4.00 °F
Average value: 0.667 J/cm Grade Count:2
Izod Impact, Unnotched 6.41 - 10.1 J/cm12.0 - 19.0 ft-lb/inAverage value: 8.26 J/cm Grade Count:12
Izod Impact, Notched (ISO) 6.50 - 10.0 kJ/m²3.09 - 4.76 ft-lb/in²Average value: 8.12 kJ/m² Grade Count:3
Charpy Impact Unnotched 2.30 - 9.00 J/cm²10.9 - 42.8 ft-lb/in²Average value: 5.10 J/cm² Grade Count:7
 1.60 - 8.50 J/cm²
@Temperature -40.0 - -20.0 °C
7.61 - 40.5 ft-lb/in²
@Temperature -40.0 - -4.00 °F
Average value: 3.94 J/cm² Grade Count:5
Charpy Impact, Notched 0.600 - 1.80 J/cm²2.86 - 8.57 ft-lb/in²Average value: 0.986 J/cm² Grade Count:6
 0.500 - 1.00 J/cm²
@Temperature -40.0 - -20.0 °C
2.38 - 4.76 ft-lb/in²
@Temperature -40.0 - -4.00 °F
Average value: 0.800 J/cm² Grade Count:3
Dart Drop, Total Energy  6.19 - 12.2 J
@Temperature -20.0 - -20.0 °C
4.57 - 9.00 ft-lb
@Temperature -4.00 - -4.00 °F
Average value: 9.19 J Grade Count:1
 6.19 - 12.2 J
@Thickness 3.18 - 3.18 mm
4.57 - 9.00 ft-lb
@Thickness 0.125 - 0.125 in
Average value: 9.19 J Grade Count:1
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 0.0100 - 100000 ohm-cm0.0100 - 100000 ohm-cmAverage value: 7290 ohm-cm Grade Count:14
Surface Resistance 10.0 - 100000 ohm10.0 - 100000 ohmAverage value: 13900 ohm Grade Count:7
 
Thermal PropertiesMetricEnglishComments
CTE, linear 6.00 - 25.0 µm/m-°C3.33 - 13.9 µin/in-°FAverage value: 16.8 µm/m-°C Grade Count:7
Melting Point 221 - 263 °C430 - 505 °FAverage value: 255 °C Grade Count:10
Deflection Temperature at 0.46 MPa (66 psi) 240 - 260 °C464 - 500 °FAverage value: 257 °C Grade Count:10
Deflection Temperature at 1.8 MPa (264 psi) 230 - 260 °C446 - 500 °FAverage value: 252 °C Grade Count:21
Vicat Softening Point 230 - 254 °C446 - 489 °FAverage value: 241 °C Grade Count:4
Flammability, UL94 HB - V-0HB - V-0Grade Count:15
 
Processing PropertiesMetricEnglishComments
Processing Temperature 270 - 300 °C518 - 572 °FAverage value: 284 °C Grade Count:5
Melt Temperature 260 - 320 °C500 - 608 °FAverage value: 286 °C Grade Count:15
Mold Temperature 60.0 - 140 °C140 - 284 °FAverage value: 88.2 °C Grade Count:20
Drying Temperature 79.4 - 107 °C175 - 225 °FAverage value: 83.6 °C Grade Count:13
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourAverage value: 3.88 hour Grade Count:8
Moisture Content 0.150 - 0.200 %0.150 - 0.200 %Average value: 0.187 % Grade Count:9
Dew Point -28.9 - -17.8 °C-20.0 - 0.000 °FAverage value: -19.6 °C Grade Count:6
Injection Pressure 30.0 - 124 MPa4350 - 18000 psiAverage value: 93.1 MPa Grade Count:13

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-44770.html

免责声明: 本文 Overview of materials for Nylon 66, 30% Carbon Fiber Filled 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4