- 密度 [g/cm3]: 0.679
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.16
- 拉伸强度 [MPa]: 40.0
- 断裂伸长率 [%]: 20.0
- 弯曲强度 [MPa]: 43.1
- 弯曲模量 [MPa]: 1.30
- 硬度: 100.0
- 热变形温度 [℃]: 160.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.679 - 1.17 g/cc | 0.0245 - 0.0423 lb/in³ | Average value: 1.14 g/cc Grade Count:63 |
| Water Absorption | 0.300 - 7.00 % | 0.300 - 7.00 % | Average value: 1.37 % Grade Count:28 |
| Moisture Absorption at Equilibrium | 1.00 - 3.00 % | 1.00 - 3.00 % | Average value: 2.05 % Grade Count:33 |
| Water Absorption at Saturation | 2.50 - 7.00 % | 2.50 - 7.00 % | Average value: 5.75 % Grade Count:48 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80.0 - 88.0 | 80.0 - 88.0 | Average value: 84.9 Grade Count:16 |
| Hardness, Rockwell R | 100 - 120 | 100 - 120 | Average value: 113 Grade Count:22 |
| Hardness, Shore D | 74.0 - 85.0 | 74.0 - 85.0 | Average value: 80.2 Grade Count:28 |
| Ball Indentation Hardness | 70.0 - 175 MPa | 10200 - 25400 psi | Average value: 140 MPa Grade Count:35 |
| Tensile Strength, Ultimate | 43.1 - 90.0 MPa | 6250 - 13100 psi | Average value: 75.5 MPa Grade Count:38 |
| Tensile Strength, Yield | 40.0 - 100 MPa | 5800 - 14500 psi | Average value: 70.8 MPa Grade Count:27 |
| Elongation at Break | 2.30 - 120 % | 2.30 - 120 % | Average value: 36.4 % Grade Count:49 |
| Elongation at Yield | 5.00 % | 5.00 % | Average value: 5.00 % Grade Count:5 |
| Creep Strength | 6.00 - 24.0 MPa | 870 - 3480 psi | Average value: 15.6 MPa Grade Count:15 |
| Modulus of Elasticity | 1.30 - 4.20 GPa | 189 - 609 ksi | Average value: 2.96 GPa Grade Count:64 |
| 0.400 - 0.800 GPa @Temperature 100 - 100 °C | 58.0 - 116 ksi @Temperature 212 - 212 °F | Average value: 0.600 GPa Grade Count:2 | |
| Flexural Yield Strength | 20.0 - 150 MPa | 2900 - 21800 psi | Average value: 96.3 MPa Grade Count:48 |
| Flexural Modulus | 1.30 - 3.70 GPa | 189 - 537 ksi | Average value: 2.81 GPa Grade Count:45 |
| Compressive Yield Strength | 6.00 - 162 MPa | 870 - 23500 psi | Average value: 66.0 MPa Grade Count:42 |
| Compressive Modulus | 1.52 - 2.76 GPa | 220 - 400 ksi | Average value: 2.28 GPa Grade Count:20 |
| Shear Strength | 44.8 - 75.8 MPa | 6500 - 11000 psi | Average value: 66.3 MPa Grade Count:15 |
| Izod Impact, Notched | 0.160 - 0.961 J/cm | 0.300 - 1.80 ft-lb/in | Average value: 0.484 J/cm Grade Count:22 |
| Izod Impact, Notched (ISO) | 2.50 - 100000 kJ/m² | 1.19 - 47600 ft-lb/in² | Average value: 11.1 kJ/m² Grade Count:19 |
| Charpy Impact Unnotched | 5.00 J/cm² - NB | 23.8 ft-lb/in² - NB | Average value: 5.63 J/cm² Grade Count:18 |
| Charpy Impact, Notched | 0.300 - 10.0 J/cm² | 1.43 - 47.6 ft-lb/in² | Average value: 1.24 J/cm² Grade Count:20 |
| Tensile Impact Strength | 72.0 kJ/m² | 34.3 ft-lb/in² | Average value: 72.0 kJ/m² Grade Count:3 |
| Coefficient of Friction | 0.0400 - 0.600 | 0.0400 - 0.600 | Average value: 0.233 Grade Count:49 |
| Coefficient of Friction, Static | 0.200 - 0.350 | 0.200 - 0.350 | Average value: 0.240 Grade Count:5 |
| Tear Strength Test | 0.150 - 1.80 | 0.150 - 1.80 | Average value: 0.375 Grade Count:14 |
| K Factor (Wear Factor) | 4.00e-11 - 1.00e-10 | 4.00e-11 - 1.00e-10 | Average value: 7.67e-11 Grade Count:12 |
| K (wear) Factor | 8.06 - 500 x 10-8 mm³/N-M | 4.00 - 248 x 10-10 in³-min/ft-lb-hr | Average value: 203 x 10-8 mm³/N-M Grade Count:12 |
| Limiting Pressure Velocity | 0.0800 - 1.33 MPa-m/sec | 2280 - 38000 psi-ft/min | Average value: 0.412 MPa-m/sec Grade Count:12 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+15 ohm-cm | 1.00e+12 - 1.00e+15 ohm-cm | Average value: 3.61e+14 ohm-cm Grade Count:39 |
| Surface Resistance | 1.00e+10 - 1.00e+13 ohm | 1.00e+10 - 1.00e+13 ohm | Average value: 4.31e+12 ohm Grade Count:35 |
| Dielectric Constant | 3.10 - 12.0 | 3.10 - 12.0 | Average value: 3.94 Grade Count:51 |
| Dielectric Strength | 15.0 - 100 kV/mm | 381 - 2540 kV/in | Average value: 27.8 kV/mm Grade Count:48 |
| Dissipation Factor | 0.00200 - 0.150 | 0.00200 - 0.150 | Average value: 0.0239 Grade Count:16 |
| Dielectric Loss Index | 0.0120 - 0.140 | 0.0120 - 0.140 | Average value: 0.0318 Grade Count:17 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:12 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 63.0 - 180 µm/m-°C | 35.0 - 100 µin/in-°F | Average value: 81.9 µm/m-°C Grade Count:62 |
| Specific Heat Capacity | 1.67 - 1.67 J/g-°C | 0.399 - 0.400 BTU/lb-°F | Average value: 1.67 J/g-°C Grade Count:17 |
| Thermal Conductivity | 0.0259 - 0.342 W/m-K | 0.180 - 2.37 BTU-in/hr-ft²-°F | Average value: 0.260 W/m-K Grade Count:41 |
| Melting Point | 190 - 238 °C | 374 - 460 °F | Average value: 219 °C Grade Count:60 |
| Maximum Service Temperature, Air | 60.0 - 180 °C | 140 - 356 °F | Average value: 131 °C Grade Count:61 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 - 221 °C | 320 - 430 °F | Average value: 203 °C Grade Count:30 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 - 204 °C | 167 - 399 °F | Average value: 117 °C Grade Count:45 |
| Minimum Service Temperature, Air | -100 - -20.0 °C | -148 - -4.00 °F | Average value: -45.1 °C Grade Count:34 |
| Glass Transition Temp, Tg | 5.00 - 50.0 °C | 41.0 - 122 °F | Average value: 39.2 °C Grade Count:5 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:32 |
| Oxygen Index | 25.0 % | 25.0 % | Average value: 25.0 % Grade Count:6 |