- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.09
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 40.0
- 断裂伸长率 [%]: 50.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 0.650
- 硬度: 116.0
- 热变形温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.71 g/cc | 0.0412 - 0.0618 lb/in³ | Average value: 1.45 g/cc Grade Count:169 |
| Filler Content | 10.0 - 44.0 % | 10.0 - 44.0 % | Average value: 32.0 % Grade Count:27 |
| Water Absorption | 0.0900 - 8.00 % | 0.0900 - 8.00 % | Average value: 3.46 % Grade Count:86 |
| Moisture Absorption at Equilibrium | 0.800 - 5.70 % | 0.800 - 5.70 % | Average value: 2.01 % Grade Count:67 |
| Water Absorption at Saturation | 3.50 - 5.00 % | 3.50 - 5.00 % | Average value: 4.26 % Grade Count:5 |
| Viscosity Measurement | 0.600 - 142 | 0.600 - 142 | Average value: 83.7 Grade Count:11 |
| Viscosity Test | 95.0 - 160 cm³/g | 95.0 - 160 cm³/g | Average value: 138 cm³/g Grade Count:9 |
| Linear Mold Shrinkage | 0.000500 - 0.0150 cm/cm | 0.000500 - 0.0150 in/in | Average value: 0.00460 cm/cm Grade Count:135 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00500 - 0.00600 cm/cm | 0.00500 - 0.00600 in/in | Average value: 0.00529 cm/cm Grade Count:7 |
| Linear Mold Shrinkage, Transverse | 0.000800 - 0.0150 cm/cm | 0.000800 - 0.0150 in/in | Average value: 0.00807 cm/cm Grade Count:56 |
| Melt Flow | 3.00 - 116 g/10 min | 3.00 - 116 g/10 min | Average value: 36.5 g/10 min Grade Count:23 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 78.0 - 94.0 | 78.0 - 94.0 | Average value: 88.0 Grade Count:4 |
| Hardness, Rockwell R | 116 - 122 | 116 - 122 | Average value: 121 Grade Count:36 |
| Ball Indentation Hardness | 90.0 - 320 MPa | 13100 - 46400 psi | Average value: 194 MPa Grade Count:5 |
| Tensile Strength, Ultimate | 45.0 - 174 MPa | 6530 - 25200 psi | Average value: 103 MPa Grade Count:130 |
| 29.0 - 178 MPa @Temperature -40.0 - 120 °C | 4210 - 25800 psi @Temperature -40.0 - 248 °F | Average value: 82.0 MPa Grade Count:6 | |
| Tensile Strength, Yield | 40.0 - 186 MPa | 5800 - 27000 psi | Average value: 101 MPa Grade Count:40 |
| Elongation at Break | 1.00 - 183 % | 1.00 - 183 % | Average value: 5.08 % Grade Count:150 |
| 2.60 - 13.0 % @Temperature -40.0 - 120 °C | 2.60 - 13.0 % @Temperature -40.0 - 248 °F | Average value: 6.66 % Grade Count:3 | |
| Elongation at Yield | 1.80 - 22.6 % | 1.80 - 22.6 % | Average value: 5.20 % Grade Count:13 |
| Modulus of Elasticity | 0.600 - 12.1 GPa | 87.0 - 1750 ksi | Average value: 6.76 GPa Grade Count:92 |
| 2.32 - 10.79 GPa @Temperature -40.0 - 120 °C | 336 - 1565 ksi @Temperature -40.0 - 248 °F | Average value: 4.84 GPa Grade Count:4 | |
| Flexural Yield Strength | 50.0 - 261 MPa | 7250 - 37800 psi | Average value: 167 MPa Grade Count:102 |
| 70.0 - 245 MPa @Temperature -40.0 - 90.0 °C | 10200 - 35500 psi @Temperature -40.0 - 194 °F | Average value: 137 MPa Grade Count:2 | |
| Flexural Modulus | 0.650 - 14.1 GPa | 94.3 - 2050 ksi | Average value: 7.33 GPa Grade Count:117 |
| 2.40 - 8.40 GPa @Temperature -40.0 - 120 °C | 348 - 1220 ksi @Temperature -40.0 - 248 °F | Average value: 4.44 GPa Grade Count:4 | |
| Compressive Yield Strength | 89.6 - 159 MPa | 13000 - 23100 psi | Average value: 119 MPa Grade Count:8 |
| Izod Impact, Notched | 0.267 - 1.85 J/cm | 0.500 - 3.47 ft-lb/in | Average value: 0.649 J/cm Grade Count:69 |
| 0.280 - 0.700 J/cm @Temperature -40.0 - -20.0 °C | 0.525 - 1.31 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.324 J/cm Grade Count:5 | |
| 0.186865 - 0.186865 J/cm @Temperature -40.0 - -40.0 °C | 0.350075 - 0.350075 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.324 J/cm Grade Count:2 | |
| 0.186865 - 0.186865 J/cm @Thickness 3.17 - 3.17 mm | 0.350075 - 0.350075 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 0.324 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 3.74 J/cm - NB | 7.00 ft-lb/in - NB | Average value: 5.76 J/cm Grade Count:17 |
| Izod Impact, Notched (ISO) | 2.40 - 16.0 kJ/m² | 1.14 - 7.61 ft-lb/in² | Average value: 5.97 kJ/m² Grade Count:51 |
| 3.00 - 10.0 kJ/m² @Temperature -40.0 - -30.0 °C | 1.43 - 4.76 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 5.66 kJ/m² Grade Count:13 | |
| Izod Impact, Unnotched (ISO) | 25.0 - 82.0 kJ/m² | 11.9 - 39.0 ft-lb/in² | Average value: 44.5 kJ/m² Grade Count:5 |
| 45.0 - 50.0 kJ/m² @Temperature -30.0 - -30.0 °C | 21.4 - 23.8 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 47.5 kJ/m² Grade Count:2 | |
| Charpy Impact Unnotched | 1.80 - 1000 J/cm² | 8.57 - 4760 ft-lb/in² | Average value: 4.92 J/cm² Grade Count:65 |
| 1.30 - 999.9 J/cm² @Temperature -40.0 - 30.0 °C | 6.19 - 4759 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 3.46 J/cm² Grade Count:41 | |
| Charpy Impact, Notched | 0.200 - 1.60 J/cm² | 0.952 - 7.61 ft-lb/in² | Average value: 0.694 J/cm² Grade Count:69 |
| 0.200 - 1.00 J/cm² @Temperature -40.0 - 30.0 °C | 0.952 - 4.76 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 0.486 J/cm² Grade Count:42 | |
| Puncture Energy | 1.50 - 1.80 J @Temperature -30.0 - -30.0 °C | 1.11 - 1.33 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.65 J Grade Count:2 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+9 - 1.00e+15 ohm-cm | 1.00e+9 - 1.00e+15 ohm-cm | Average value: 2.33e+14 ohm-cm Grade Count:69 |
| Surface Resistance | 1.00e+10 - 1.00e+16 ohm | 1.00e+10 - 1.00e+16 ohm | Average value: 3.70e+14 ohm Grade Count:32 |
| Dielectric Constant | 3.00 - 14.0 | 3.00 - 14.0 | Average value: 5.37 Grade Count:48 |
| Dielectric Strength | 11.8 - 90.0 kV/mm | 300 - 2290 kV/in | Average value: 27.7 kV/mm Grade Count:49 |
| Dissipation Factor | 0.00500 - 0.400 | 0.00500 - 0.400 | Average value: 0.0923 Grade Count:35 |
| Dielectric Loss Index | 0.0200 - 0.200 | 0.0200 - 0.200 | Average value: 0.110 Grade Count:6 |
| Arc Resistance | 100 - 130 sec | 100 - 130 sec | Average value: 119 sec Grade Count:6 |
| Comparative Tracking Index | 300 - 600 V | 300 - 600 V | Average value: 499 V Grade Count:40 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.300 - 500 µm/m-°C | 0.167 - 278 µin/in-°F | Average value: 50.8 µm/m-°C Grade Count:51 |
| CTE, linear, Transverse to Flow | 0.340 - 100 µm/m-°C | 0.189 - 55.6 µin/in-°F | Average value: 63.0 µm/m-°C Grade Count:23 |
| Specific Heat Capacity | 1.30 - 2.03 J/g-°C | 0.311 - 0.485 BTU/lb-°F | Average value: 1.43 J/g-°C Grade Count:7 |
| Thermal Conductivity | 0.250 - 1.00 W/m-K | 1.74 - 6.94 BTU-in/hr-ft²-°F | Average value: 0.533 W/m-K Grade Count:9 |
| Melting Point | 205 - 295 °C | 401 - 563 °F | Average value: 221 °C Grade Count:120 |
| Maximum Service Temperature, Air | 80.0 - 200 °C | 176 - 392 °F | Average value: 156 °C Grade Count:14 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 - 265 °C | 167 - 509 °F | Average value: 211 °C Grade Count:78 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 220 °C | 131 - 428 °F | Average value: 191 °C Grade Count:134 |
| Deflection Temperature at 8.0 MPa | 50.0 - 140 °C | 122 - 284 °F | Average value: 82.5 °C Grade Count:6 |
| Vicat Softening Point | 165 - 221 °C | 329 - 430 °F | Average value: 201 °C Grade Count:18 |
| UL RTI, Electrical | 65.0 °C | 149 °F | Average value: 65.0 °C Grade Count:3 |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | Average value: 65.0 °C Grade Count:3 |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | Average value: 65.0 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:69 |
| Oxygen Index | 22.0 - 68.0 % | 22.0 - 68.0 % | Average value: 39.1 % Grade Count:7 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 819 °C Grade Count:12 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 300 °C | 176 - 572 °F | Average value: 253 °C Grade Count:17 |
| Feed Temperature | 60.0 - 240 °C | 140 - 464 °F | Average value: 166 °C Grade Count:5 |
| Nozzle Temperature | 210 - 285 °C | 410 - 545 °F | Average value: 259 °C Grade Count:7 |
| Melt Temperature | 216 - 330 °C | 420 - 626 °F | Average value: 264 °C Grade Count:58 |
| Mold Temperature | 50.0 - 140 °C | 122 - 284 °F | Average value: 84.8 °C Grade Count:63 |
| Drying Temperature | 75.0 - 110 °C | 167 - 230 °F | Average value: 84.9 °C Grade Count:30 |
| Dry Time | 2.00 - 5.00 hour | 2.00 - 5.00 hour | Average value: 3.39 hour Grade Count:23 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:2 | |
| Moisture Content | 0.0300 - 2.20 % | 0.0300 - 2.20 % | Average value: 0.217 % Grade Count:26 |
| Injection Pressure | 4.96 - 138 MPa | 720 - 20000 psi | Average value: 77.2 MPa Grade Count:25 |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi | Average value: 0.299 MPa Grade Count:6 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 69.0 rpm Grade Count:5 |