Overview of materials for Nylon 6, Heat Stabilized

Overview of materials for Nylon 6, Heat Stabilized 物性表: Overview of materials for Nylon 6, Heat Stabilized物性表及特性介绍,Overview of materials for Nylon 6, Heat Stabilized注塑参数详情,如需Overview of materials for Nylon 6, Heat Stabilized下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 1.0
  • 密度 [g/cm3]: 1.04
  • 吸水率 [%]: 0.2
  • 缺口冲击强度: 0.3
  • 拉伸强度 [MPa]: 29.0
  • 断裂伸长率 [%]: 9.65
  • 弯曲强度 [MPa]: 37.9
  • 弯曲模量 [MPa]: 0.469
  • 硬度: 70.0
  • 热变形温度 [℃]: 95.0
 
Physical PropertiesMetricEnglishComments
Density 1.04 - 1.70 g/cc0.0376 - 0.0614 lb/in³Average value: 1.27 g/cc Grade Count:234
Filler Content 13.0 - 40.0 %13.0 - 40.0 %Average value: 32.2 % Grade Count:10
Water Absorption 0.200 - 10.0 %0.200 - 10.0 %Average value: 1.36 % Grade Count:157
Moisture Absorption at Equilibrium 0.250 - 2.80 %0.250 - 2.80 %Average value: 2.12 % Grade Count:28
Water Absorption at Saturation 6.00 - 9.80 %6.00 - 9.80 %Average value: 7.71 % Grade Count:16
Viscosity Measurement 0.300 - 2000.300 - 200Average value: 33.8 Grade Count:15
Linear Mold Shrinkage 0.00130 - 0.0350 cm/cm0.00130 - 0.0350 in/inAverage value: 0.00779 cm/cm Grade Count:198
Linear Mold Shrinkage, Transverse 0.00500 - 0.0183 cm/cm0.00500 - 0.0183 in/inAverage value: 0.0115 cm/cm Grade Count:38
Melt Flow 1.00 - 100 g/10 min1.00 - 100 g/10 minAverage value: 12.3 g/10 min Grade Count:16
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 70.0 - 21270.0 - 212Average value: 115 Grade Count:122
Ball Indentation Hardness 75.0 - 175 MPa10900 - 25400 psiAverage value: 138 MPa Grade Count:12
Tensile Strength, Ultimate 37.9 - 200 MPa5500 - 29000 psiAverage value: 98.3 MPa Grade Count:56
 21.0 - 60.0 MPa
@Temperature 60.0 - 120 °C		3050 - 8700 psi
@Temperature 140 - 248 °F		Average value: 40.2 MPa Grade Count:2
Tensile Strength, Yield 29.0 - 234 MPa4200 - 34000 psiAverage value: 105 MPa Grade Count:184
Elongation at Break 1.50 - 350 %1.50 - 350 %Average value: 40.2 % Grade Count:203
Elongation at Yield 2.00 - 200 %2.00 - 200 %Average value: 12.6 % Grade Count:23
Creep Strength 4.00 - 20.0 MPa580 - 2900 psiAverage value: 11.9 MPa Grade Count:10
Modulus of Elasticity 0.470 - 15.0 GPa68.2 - 2180 ksiAverage value: 5.16 GPa Grade Count:54
Flexural Yield Strength 9.65 - 352 MPa1400 - 51000 psiAverage value: 147 MPa Grade Count:211
Flexural Modulus 0.469 - 20.0 GPa68.0 - 2900 ksiAverage value: 4.84 GPa Grade Count:216
 0.450 - 3.70 GPa
@Temperature 60.0 - 120 °C		65.3 - 537 ksi
@Temperature 140 - 248 °F		Average value: 1.54 GPa Grade Count:2
Compressive Yield Strength 29.0 - 147 MPa4210 - 21300 psiAverage value: 66.6 MPa Grade Count:12
Poissons Ratio 0.3500.350Average value: 0.350 Grade Count:4
Izod Impact, Notched 0.300 - 5340 J/cm0.562 - 10000 ft-lb/inAverage value: 1.48 J/cm Grade Count:176
 0.250 - 0.300 J/cm
@Temperature -40.0 - -20.0 °C		0.468 - 0.562 ft-lb/in
@Temperature -40.0 - -4.00 °F		Average value: 1.44 J/cm Grade Count:2
 0.186865 - 5338.47 J/cm
@Temperature -40.0 - -20.0 °C		0.350075 - 10001.1 ft-lb/in
@Temperature -40.0 - -4.00 °F		Average value: 1.44 J/cm Grade Count:19
 0.186865 - 5338.47 J/cm
@Thickness 1.57 - 3.17 mm		0.350075 - 10001.1 ft-lb/in
@Thickness 0.0618 - 0.125 in		Average value: 1.44 J/cm Grade Count:19
Izod Impact, Unnotched 3.20 - 5340 J/cm6.00 - 10000 ft-lb/inAverage value: 9.90 J/cm Grade Count:46
Izod Impact, Notched (ISO) 2.50 - 100000 kJ/m²1.19 - 47600 ft-lb/in²Average value: 15.3 kJ/m² Grade Count:28
 5.00 - 20.0 kJ/m²
@Temperature -30.0 - -30.0 °C		2.38 - 9.52 ft-lb/in²
@Temperature -22.0 - -22.0 °F		Average value: 10.9 kJ/m² Grade Count:14
Izod Impact, Unnotched (ISO) 30.0 - 110 kJ/m²14.3 - 52.3 ft-lb/in²Average value: 66.5 kJ/m² Grade Count:10
 30.0 - 100 kJ/m²
@Temperature -30.0 - -30.0 °C		14.3 - 47.6 ft-lb/in²
@Temperature -22.0 - -22.0 °F		Average value: 55.8 kJ/m² Grade Count:10
Charpy Impact Unnotched 2.00 J/cm² - NB9.52 ft-lb/in² - NBAverage value: 6.58 J/cm² Grade Count:29
 1.50 J/cm² - NB
@Temperature -40.0 - -20.0 °C		7.14 ft-lb/in² - NB
@Temperature -40.0 - -4.00 °F		Average value: 4.89 J/cm² Grade Count:24
Charpy Impact, Notched 0.150 - 13.0 J/cm²0.714 - 61.9 ft-lb/in²Average value: 1.65 J/cm² Grade Count:28
 0.150 - 2.00 J/cm²
@Temperature -30.0 - -20.0 °C		0.714 - 9.52 ft-lb/in²
@Temperature -22.0 - -4.00 °F		Average value: 0.804 J/cm² Grade Count:24
Puncture Energy 64.0 - 64.0 J
@Temperature -30.0 - -30.0 °C		47.2 - 47.2 ft-lb
@Temperature -22.0 - -22.0 °F		Average value: 64.0 J Grade Count:1
Coefficient of Friction 0.0400 - 0.3900.0400 - 0.390Average value: 0.204 Grade Count:14
Tear Strength Test 0.150 - 0.2500.150 - 0.250Average value: 0.190 Grade Count:10
K Factor (Wear Factor) 9.00e-11 - 0.4409.00e-11 - 0.440Average value: 0.0400 Grade Count:11
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 1.00 - 5.00e+15 ohm-cm1.00 - 5.00e+15 ohm-cmAverage value: 5.85e+14 ohm-cm Grade Count:143
Surface Resistance 1.00 - 1.00e+15 ohm1.00 - 1.00e+15 ohmAverage value: 1.01e+14 ohm Grade Count:48
Dielectric Constant 3.00 - 4.003.00 - 4.00Average value: 3.63 Grade Count:15
Dielectric Strength 15.4 - 80.0 kV/mm390 - 2030 kV/inAverage value: 20.3 kV/mm Grade Count:132
Dielectric Loss Index 0.03000.0300Average value: 0.0300 Grade Count:10
Comparative Tracking Index 400 - 600 V400 - 600 VAverage value: 566 V Grade Count:23
 
Thermal PropertiesMetricEnglishComments
CTE, linear 7.20 - 150 µm/m-°C4.00 - 83.3 µin/in-°FAverage value: 49.9 µm/m-°C Grade Count:139
CTE, linear, Transverse to Flow 90.0 - 150 µm/m-°C50.0 - 83.3 µin/in-°FAverage value: 108 µm/m-°C Grade Count:5
Specific Heat Capacity 1.67 J/g-°C0.399 BTU/lb-°FAverage value: 1.67 J/g-°C Grade Count:10
Thermal Conductivity 0.250 W/m-K1.74 BTU-in/hr-ft²-°FAverage value: 0.250 W/m-K Grade Count:10
Melting Point 215 - 260 °C419 - 500 °FAverage value: 221 °C Grade Count:79
Maximum Service Temperature, Air 115 - 190 °C239 - 374 °FAverage value: 149 °C Grade Count:13
Deflection Temperature at 0.46 MPa (66 psi) 95.0 - 221 °C203 - 430 °FAverage value: 199 °C Grade Count:150
Deflection Temperature at 1.8 MPa (264 psi) 49.0 - 250 °C120 - 482 °FAverage value: 142 °C Grade Count:209
Vicat Softening Point 190 - 255 °C374 - 491 °FAverage value: 206 °C Grade Count:29
Minimum Service Temperature, Air -100 - -40.0 °C-148 - -40.0 °FAverage value: -45.0 °C Grade Count:11
UL RTI, Electrical 120 °C248 °FAverage value: 120 °C Grade Count:3
UL RTI, Mechanical with Impact 120 °C248 °FAverage value: 120 °C Grade Count:3
UL RTI, Mechanical without Impact 115 °C239 °FAverage value: 115 °C Grade Count:3
Flammability, UL94 HB - 5VBHB - 5VBGrade Count:108
Oxygen Index 26.0 - 30.0 %26.0 - 30.0 %Average value: 28.3 % Grade Count:3
Glow Wire Test 192 - 960 °C378 - 1760 °FAverage value: 788 °C Grade Count:21
Shrinkage 0.0700 - 0.200 %0.0700 - 0.200 %Average value: 0.143 % Grade Count:5
 
Processing PropertiesMetricEnglishComments
Processing Temperature 230 - 275 °C446 - 527 °FAverage value: 249 °C Grade Count:26
Feed Temperature 60.0 - 80.0 °C140 - 176 °FAverage value: 70.0 °C Grade Count:10
Nozzle Temperature 227 - 293 °C440 - 560 °FAverage value: 251 °C Grade Count:13
Melt Temperature 138 - 293 °C280 - 560 °FAverage value: 254 °C Grade Count:73
Mold Temperature 21.1 - 121 °C70.0 - 250 °FAverage value: 78.7 °C Grade Count:84
Drying Temperature 73.9 - 100 °C165 - 212 °FAverage value: 78.6 °C Grade Count:67
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourAverage value: 3.29 hour Grade Count:52
 2.00 - 6.00 hour
@Temperature 79.4 - 80.0 °C		2.00 - 6.00 hour
@Temperature 175 - 176 °F		Average value: 3.42 hour Grade Count:19
Moisture Content 0.000 - 0.200 %0.000 - 0.200 %Average value: 0.157 % Grade Count:59
Injection Pressure 3.45 - 172 MPa500 - 25000 psiAverage value: 43.8 MPa Grade Count:34
Hold Pressure 50.0 - 100 MPa7250 - 14500 psiAverage value: 75.0 MPa Grade Count:10
Back Pressure 0.000 - 1.72 MPa0.000 - 250 psiAverage value: 0.450 MPa Grade Count:37
Shot Size 30.0 - 80.0 %30.0 - 80.0 %Average value: 55.0 % Grade Count:13
Screw Speed 20.0 - 120 rpm20.0 - 120 rpmAverage value: 73.9 rpm Grade Count:37

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45774.html

免责声明: 本文 Overview of materials for Nylon 6, Heat Stabilized 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4