  4. DuPont Performance Polymers Zytel® 153HSL NC010 Nylon 612

DuPont Performance Polymers Zytel® 153HSL NC010 Nylon 612

DuPont Performance Polymers Zytel® 153HSL NC010 Nylon 612 物性表: DuPont Performance Polymers Zytel® 153HSL NC010 Nylon 612物性表及特性介绍,DuPont Performance Polymers Zytel® 153HSL NC010 Nylon 612注塑参数详情,如需DuPont Performance Polymers Zytel® 153HSL NC010 Nylon 612下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.06
  • 吸水率 [%]: 0.25
  • 缺口冲击强度: 0.32
  • 拉伸强度 [MPa]: 30.0
  • 弯曲模量 [MPa]: 0.410
  • 硬度: 114.0
  • 热变形温度 [℃]: 135.0
  • 脆化温度 [℃]: -126.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.06 g/cc1.06 g/ccDAM; ASTM D792
Density 1.06 g/cc0.0383 lb/in³DAM; ISO 1183
Water Absorption  0.25 %
@Temperature 23.0 °C		0.25 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 1.3 %
@Temperature 23.0 °C		1.3 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage 0.011 cm/cm
@Thickness 3.20 mm		0.011 in/in
@Thickness 0.126 in		Flow; DAM
Linear Mold Shrinkage, Flow 0.013 cm/cm
@Thickness 2.00 mm		0.013 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 114114DAM; ASTM D785
Tensile Strength  41.0 MPa
@Temperature 77.0 °C		5950 psi
@Temperature 171 °F		DAM; ASTM D638
 61.0 MPa
@Temperature 23.0 °C		8850 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 61.0 MPa
@Temperature 23.0 °C		8850 psi
@Temperature 73.4 °F		DAM; ASTM D638
 94.0 MPa
@Temperature -40.0 °C		13600 psi
@Temperature -40.0 °F		DAM; ASTM D638
 94.0 MPa
@Temperature -40.0 °C		13600 psi
@Temperature -40.0 °F		50%RH; ASTM D638
Tensile Stress  10.64 MPa
@Strain 3.83 %,
Temperature 120 °C		1543 psi
@Strain 3.83 %,
Temperature 248 °F		DAM; ISO 527
 10.69 MPa
@Strain 3.00 %,
Temperature 120 °C		1550 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 527
 12.05 MPa
@Strain 0.490 %,
Temperature 23.0 °C		1748 psi
@Strain 0.490 %,
Temperature 73.4 °F		DAM; ISO 527
 13.32 MPa
@Strain 3.00 %,
Temperature 90.0 °C		1932 psi
@Strain 3.00 %,
Temperature 194 °F		50%RH; ISO 527
 13.4 MPa
@Strain 3.43 %,
Temperature 90.0 °C		1940 psi
@Strain 3.43 %,
Temperature 194 °F		DAM; ISO 527
 14.35 MPa
@Strain 2.62 %,
Temperature 60.0 °C		2081 psi
@Strain 2.62 %,
Temperature 140 °F		50%RH; ISO 527
 14.43 MPa
@Strain 7.06 %,
Temperature 120 °C		2093 psi
@Strain 7.06 %,
Temperature 248 °F		DAM; ISO 527
 15.48 MPa
@Strain 5.80 %,
Temperature 120 °C		2245 psi
@Strain 5.80 %,
Temperature 248 °F		50%RH; ISO 527
 16.83 MPa
@Strain 10.69 %,
Temperature 120 °C		2441 psi
@Strain 10.69 %,
Temperature 248 °F		DAM; ISO 527
 17.88 MPa
@Strain 8.60 %,
Temperature 120 °C		2593 psi
@Strain 8.60 %,
Temperature 248 °F		50%RH; ISO 527
 18.15 MPa
@Strain 13.91 %,
Temperature 120 °C		2632 psi
@Strain 13.91 %,
Temperature 248 °F		DAM; ISO 527
 19.09 MPa
@Strain 17.54 %,
Temperature 120 °C		2769 psi
@Strain 17.54 %,
Temperature 248 °F		DAM; ISO 527
 19.18 MPa
@Strain 6.65 %,
Temperature 90.0 °C		2782 psi
@Strain 6.65 %,
Temperature 194 °F		DAM; ISO 527
 19.37 MPa
@Strain 11.8 %,
Temperature 120 °C		2809 psi
@Strain 11.8 %,
Temperature 248 °F		50%RH; ISO 527
 19.6 MPa
@Strain 3.02 %,
Temperature 40.0 °C		2840 psi
@Strain 3.02 %,
Temperature 104 °F		50%RH; ISO 527
 19.72 MPa
@Strain 21.17 %,
Temperature 120 °C		2860 psi
@Strain 21.17 %,
Temperature 248 °F		DAM; ISO 527
 19.79 MPa
@Strain 3.80 %,
Temperature 60.0 °C		2870 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 527
 19.85 MPa
@Strain 5.80 %,
Temperature 90.0 °C		2879 psi
@Strain 5.80 %,
Temperature 194 °F		50%RH; ISO 527
 20.11 MPa
@Strain 14.6 %,
Temperature 120 °C		2917 psi
@Strain 14.6 %,
Temperature 248 °F		50%RH; ISO 527
 20.12 MPa
@Strain 24.4 %,
Temperature 120 °C		2918 psi
@Strain 24.4 %,
Temperature 248 °F		DAM; ISO 527
 20.47 MPa
@Strain 28.03 %,
Temperature 120 °C		2969 psi
@Strain 28.03 %,
Temperature 248 °F		DAM; ISO 527
 20.59 MPa
@Strain 17.4 %,
Temperature 120 °C		2986 psi
@Strain 17.4 %,
Temperature 248 °F		50%RH; ISO 527
 20.73 MPa
@Strain 31.25 %,
Temperature 120 °C		3007 psi
@Strain 31.25 %,
Temperature 248 °F		DAM; ISO 527
 20.89 MPa
@Strain 20.2 %,
Temperature 120 °C		3030 psi
@Strain 20.2 %,
Temperature 248 °F		50%RH; ISO 527
 20.96 MPa
@Strain 34.88 %,
Temperature 120 °C		3040 psi
@Strain 34.88 %,
Temperature 248 °F		DAM; ISO 527
 21.11 MPa
@Strain 23.0 %,
Temperature 120 °C		3062 psi
@Strain 23.0 %,
Temperature 248 °F		50%RH; ISO 527
 21.24 MPa
@Strain 25.8 %,
Temperature 120 °C		3081 psi
@Strain 25.8 %,
Temperature 248 °F		50%RH; ISO 527
 21.4 MPa
@Strain 29.0 %,
Temperature 120 °C		3100 psi
@Strain 29.0 %,
Temperature 248 °F		50%RH; ISO 527
 22.62 MPa
@Strain 10.28 %,
Temperature 90.0 °C		3281 psi
@Strain 10.28 %,
Temperature 194 °F		DAM; ISO 527
 23.04 MPa
@Strain 5.44 %,
Temperature 60.0 °C		3342 psi
@Strain 5.44 %,
Temperature 140 °F		50%RH; ISO 527
 23.54 MPa
@Strain 8.60 %,
Temperature 90.0 °C		3414 psi
@Strain 8.60 %,
Temperature 194 °F		50%RH; ISO 527
 24.39 MPa
@Strain 13.51 %,
Temperature 90.0 °C		3537 psi
@Strain 13.51 %,
Temperature 194 °F		DAM; ISO 527
 25.52 MPa
@Strain 16.73 %,
Temperature 90.0 °C		3701 psi
@Strain 16.73 %,
Temperature 194 °F		DAM; ISO 527
 25.74 MPa
@Strain 11.4 %,
Temperature 90.0 °C		3733 psi
@Strain 11.4 %,
Temperature 194 °F		50%RH; ISO 527
 26.22 MPa
@Strain 1.14 %,
Temperature 23.0 °C		3803 psi
@Strain 1.14 %,
Temperature 73.4 °F		DAM; ISO 527
 26.27 MPa
@Strain 19.96 %,
Temperature 90.0 °C		3810 psi
@Strain 19.96 %,
Temperature 194 °F		DAM; ISO 527
 26.86 MPa
@Strain 23.59 %,
Temperature 90.0 °C		3896 psi
@Strain 23.59 %,
Temperature 194 °F		DAM; ISO 527
 27.06 MPa
@Strain 14.2 %,
Temperature 90.0 °C		3925 psi
@Strain 14.2 %,
Temperature 194 °F		50%RH; ISO 527
 27.2 MPa
@Strain 26.82 %,
Temperature 90.0 °C		3950 psi
@Strain 26.82 %,
Temperature 194 °F		DAM; ISO 527
 27.43 MPa
@Strain 30.04 %,
Temperature 90.0 °C		3978 psi
@Strain 30.04 %,
Temperature 194 °F		DAM; ISO 527
 27.61 MPa
@Strain 33.27 %,
Temperature 90.0 °C		4004 psi
@Strain 33.27 %,
Temperature 194 °F		DAM; ISO 527
 27.63 MPa
@Strain 7.86 %,
Temperature 60.0 °C		4007 psi
@Strain 7.86 %,
Temperature 140 °F		50%RH; ISO 527
 27.76 MPa
@Strain 16.6 %,
Temperature 90.0 °C		4026 psi
@Strain 16.6 %,
Temperature 194 °F		50%RH; ISO 527
 27.86 MPa
@Strain 5.44 %,
Temperature 40.0 °C		4041 psi
@Strain 5.44 %,
Temperature 104 °F		50%RH; ISO 527
 27.96 MPa
@Strain 7.80 %,
Temperature 60.0 °C		4055 psi
@Strain 7.80 %,
Temperature 140 °F		DAM; ISO 527
 28.22 MPa
@Strain 19.4 %,
Temperature 90.0 °C		4093 psi
@Strain 19.4 %,
Temperature 194 °F		50%RH; ISO 527
 28.4 MPa
@Strain 2.60 %,
Temperature 23.0 °C		4120 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 527
 28.47 MPa
@Strain 22.2 %,
Temperature 90.0 °C		4129 psi
@Strain 22.2 %,
Temperature 194 °F		50%RH; ISO 527
 28.6 MPa
@Strain 25.0 %,
Temperature 90.0 °C		4150 psi
@Strain 25.0 %,
Temperature 194 °F		50%RH; ISO 527
 28.63 MPa
@Strain 27.8 %,
Temperature 90.0 °C		4152 psi
@Strain 27.8 %,
Temperature 194 °F		50%RH; ISO 527
 30.04 MPa
@Strain 3.02 %,
Temperature 40.0 °C		4357 psi
@Strain 3.02 %,
Temperature 104 °F		DAM; ISO 527
 30.98 MPa
@Strain 10.69 %,
Temperature 60.0 °C		4493 psi
@Strain 10.69 %,
Temperature 140 °F		50%RH; ISO 527
 31.72 MPa
@Strain 11.4 %,
Temperature 60.0 °C		4601 psi
@Strain 11.4 %,
Temperature 140 °F		DAM; ISO 527
 32.84 MPa
@Strain 13.11 %,
Temperature 60.0 °C		4763 psi
@Strain 13.11 %,
Temperature 140 °F		50%RH; ISO 527
 33.21 MPa
@Strain 1.47 %,
Temperature 23.0 °C		4817 psi
@Strain 1.47 %,
Temperature 73.4 °F		DAM; ISO 527
 33.84 MPa
@Strain 15.0 %,
Temperature 60.0 °C		4908 psi
@Strain 15.0 %,
Temperature 140 °F		DAM; ISO 527
 33.87 MPa
@Strain 8.27 %,
Temperature 40.0 °C		4912 psi
@Strain 8.27 %,
Temperature 104 °F		50%RH; ISO 527
 34.24 MPa
@Strain 15.93 %,
Temperature 60.0 °C		4966 psi
@Strain 15.93 %,
Temperature 140 °F		50%RH; ISO 527
 34.98 MPa
@Strain 18.35 %,
Temperature 60.0 °C		5073 psi
@Strain 18.35 %,
Temperature 140 °F		50%RH; ISO 527
 35.03 MPa
@Strain 18.6 %,
Temperature 60.0 °C		5081 psi
@Strain 18.6 %,
Temperature 140 °F		DAM; ISO 527
 35.5 MPa
@Strain 21.17 %,
Temperature 60.0 °C		5150 psi
@Strain 21.17 %,
Temperature 140 °F		50%RH; ISO 527
 35.73 MPa
@Strain 23.59 %,
Temperature 60.0 °C		5182 psi
@Strain 23.59 %,
Temperature 140 °F		50%RH; ISO 527
 35.83 MPa
@Strain 26.41 %,
Temperature 60.0 °C		5197 psi
@Strain 26.41 %,
Temperature 140 °F		50%RH; ISO 527
 35.85 MPa
@Strain 22.6 %,
Temperature 60.0 °C		5200 psi
@Strain 22.6 %,
Temperature 140 °F		DAM; ISO 527
 36.19 MPa
@Strain 5.44 %,
Temperature 40.0 °C		5249 psi
@Strain 5.44 %,
Temperature 104 °F		DAM; ISO 527
 36.29 MPa
@Strain 26.2 %,
Temperature 60.0 °C		5263 psi
@Strain 26.2 %,
Temperature 140 °F		DAM; ISO 527
 36.62 MPa
@Strain 29.8 %,
Temperature 60.0 °C		5311 psi
@Strain 29.8 %,
Temperature 140 °F		DAM; ISO 527
 36.8 MPa
@Strain 33.8 %,
Temperature 60.0 °C		5340 psi
@Strain 33.8 %,
Temperature 140 °F		DAM; ISO 527
 36.9 MPa
@Strain 37.4 %,
Temperature 60.0 °C		5350 psi
@Strain 37.4 %,
Temperature 140 °F		DAM; ISO 527
 37.33 MPa
@Strain 5.00 %,
Temperature 23.0 °C		5414 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 527
 37.63 MPa
@Strain 11.09 %,
Temperature 40.0 °C		5458 psi
@Strain 11.09 %,
Temperature 104 °F		50%RH; ISO 527
 39.71 MPa
@Strain 13.51 %,
Temperature 40.0 °C		5759 psi
@Strain 13.51 %,
Temperature 104 °F		50%RH; ISO 527
 40.35 MPa
@Strain 8.27 %,
Temperature 40.0 °C		5852 psi
@Strain 8.27 %,
Temperature 104 °F		DAM; ISO 527
 41.33 MPa
@Strain 16.33 %,
Temperature 40.0 °C		5994 psi
@Strain 16.33 %,
Temperature 104 °F		50%RH; ISO 527
 42.32 MPa
@Strain 19.15 %,
Temperature 40.0 °C		6138 psi
@Strain 19.15 %,
Temperature 104 °F		50%RH; ISO 527
 42.85 MPa
@Strain 21.57 %,
Temperature 40.0 °C		6215 psi
@Strain 21.57 %,
Temperature 104 °F		50%RH; ISO 527
 43.05 MPa
@Strain 7.40 %,
Temperature 23.0 °C		6244 psi
@Strain 7.40 %,
Temperature 73.4 °F		50%RH; ISO 527
 43.09 MPa
@Strain 11.09 %,
Temperature 40.0 °C		6250 psi
@Strain 11.09 %,
Temperature 104 °F		DAM; ISO 527
 43.18 MPa
@Strain 24.4 %,
Temperature 40.0 °C		6263 psi
@Strain 24.4 %,
Temperature 104 °F		50%RH; ISO 527
 43.33 MPa
@Strain 27.22 %,
Temperature 40.0 °C		6284 psi
@Strain 27.22 %,
Temperature 104 °F		50%RH; ISO 527
 44.23 MPa
@Strain 2.12 %,
Temperature 23.0 °C		6415 psi
@Strain 2.12 %,
Temperature 73.4 °F		DAM; ISO 527
 44.76 MPa
@Strain 13.91 %,
Temperature 40.0 °C		6492 psi
@Strain 13.91 %,
Temperature 104 °F		DAM; ISO 527
 45.7 MPa
@Strain 16.33 %,
Temperature 40.0 °C		6630 psi
@Strain 16.33 %,
Temperature 104 °F		DAM; ISO 527
 46.39 MPa
@Strain 19.15 %,
Temperature 40.0 °C		6728 psi
@Strain 19.15 %,
Temperature 104 °F		DAM; ISO 527
 46.81 MPa
@Strain 21.98 %,
Temperature 40.0 °C		6789 psi
@Strain 21.98 %,
Temperature 104 °F		DAM; ISO 527
 47.03 MPa
@Strain 24.4 %,
Temperature 40.0 °C		6821 psi
@Strain 24.4 %,
Temperature 104 °F		DAM; ISO 527
 47.15 MPa
@Strain 27.22 %,
Temperature 40.0 °C		6839 psi
@Strain 27.22 %,
Temperature 104 °F		DAM; ISO 527
 47.43 MPa
@Strain 10.2 %,
Temperature 23.0 °C		6879 psi
@Strain 10.2 %,
Temperature 73.4 °F		50%RH; ISO 527
 49.11 MPa
@Strain 2.45 %,
Temperature 23.0 °C		7123 psi
@Strain 2.45 %,
Temperature 73.4 °F		DAM; ISO 527
 49.93 MPa
@Strain 12.6 %,
Temperature 23.0 °C		7242 psi
@Strain 12.6 %,
Temperature 73.4 °F		50%RH; ISO 527
 51.61 MPa
@Strain 15.0 %,
Temperature 23.0 °C		7485 psi
@Strain 15.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 52.66 MPa
@Strain 17.4 %,
Temperature 23.0 °C		7638 psi
@Strain 17.4 %,
Temperature 73.4 °F		50%RH; ISO 527
 52.78 MPa
@Strain 2.78 %,
Temperature 23.0 °C		7655 psi
@Strain 2.78 %,
Temperature 73.4 °F		DAM; ISO 527
 53.3 MPa
@Strain 19.8 %,
Temperature 23.0 °C		7730 psi
@Strain 19.8 %,
Temperature 73.4 °F		50%RH; ISO 527
 53.66 MPa
@Strain 22.2 %,
Temperature 23.0 °C		7783 psi
@Strain 22.2 %,
Temperature 73.4 °F		50%RH; ISO 527
 53.79 MPa
@Strain 24.6 %,
Temperature 23.0 °C		7802 psi
@Strain 24.6 %,
Temperature 73.4 °F		50%RH; ISO 527
 56.99 MPa
@Strain 3.43 %,
Temperature 23.0 °C		8266 psi
@Strain 3.43 %,
Temperature 73.4 °F		DAM; ISO 527
 57.81 MPa
@Strain 3.76 %,
Temperature 23.0 °C		8385 psi
@Strain 3.76 %,
Temperature 73.4 °F		DAM; ISO 527
 58.38 MPa
@Strain 4.41 %,
Temperature 23.0 °C		8467 psi
@Strain 4.41 %,
Temperature 73.4 °F		DAM; ISO 527
 58.39 MPa
@Strain 4.74 %,
Temperature 23.0 °C		8469 psi
@Strain 4.74 %,
Temperature 73.4 °F		DAM; ISO 527
Tensile Strength, Yield  30.0 MPa
@Temperature 77.0 °C		4350 psi
@Temperature 171 °F		DAM; ASTM D638
 51.0 MPa
@Temperature 23.0 °C		7400 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 53.0 MPa
@Temperature 23.0 °C		7690 psi
@Temperature 73.4 °F		50%RH; ISO 527
 61.0 MPa
@Temperature 23.0 °C		8850 psi
@Temperature 73.4 °F		DAM; ASTM D638
 62.0 MPa
@Temperature 23.0 °C		8990 psi
@Temperature 73.4 °F		DAM; ISO 527
 93.0 MPa
@Temperature -40.0 °C		13500 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 94.0 MPa
@Temperature -40.0 °C		13600 psi
@Temperature -40.0 °F		DAM; ASTM D638
Elongation at Break  15 %
@Temperature -40.0 °C		15 %
@Temperature -40.0 °F		DAM; ASTM D638
 30 %
@Temperature -40.0 °C		30 %
@Temperature -40.0 °F		50%RH; ASTM D638
 30 %
@Temperature 23.0 °C		30 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 150 %
@Temperature 23.0 °C		150 %
@Temperature 73.4 °F		DAM; ASTM D638
 >= 300 %
@Temperature 23.0 °C		>= 300 %
@Temperature 73.4 °F		50%RH; ASTM D638
Elongation at Yield  4.4 %
@Temperature 23.0 °C		4.4 %
@Temperature 73.4 °F		DAM; ISO 527
 7.0 %
@Temperature 23.0 °C		7.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 8.0 %
@Temperature -40.0 °C		8.0 %
@Temperature -40.0 °F		DAM; ASTM D638
 14 %
@Temperature -40.0 °C		14 %
@Temperature -40.0 °F		50%RH; ASTM D638
 19 %
@Temperature 23.0 °C		19 %
@Temperature 73.4 °F		50%RH; ISO 527
 30 %
@Temperature 77.0 °C		30 %
@Temperature 171 °F		DAM; ASTM D638
 40 %
@Temperature 23.0 °C		40 %
@Temperature 73.4 °F		50%RH; ASTM D638
Tensile Modulus  1.60 GPa
@Temperature 23.0 °C		232 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 2.40 GPa
@Temperature 23.0 °C		348 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  0.410 GPa
@Temperature 77.0 °C		59.5 ksi
@Temperature 171 °F		DAM; ASTM D790
 1.24 GPa
@Temperature 23.0 °C		180 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 1.45 GPa
@Temperature 23.0 °C		210 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 2.03 GPa
@Temperature 23.0 °C		294 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 2.10 GPa
@Temperature 23.0 °C		305 ksi
@Temperature 73.4 °F		DAM; ISO 178
 2.30 GPa
@Temperature -40.0 °C		334 ksi
@Temperature -40.0 °F		DAM; ASTM D790
 2.80 GPa
@Temperature -40.0 °C		406 ksi
@Temperature -40.0 °F		50%RH; ASTM D790
Shear Strength 59.0 MPa
@Temperature 23.0 °C		8560 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.320 J/cm
@Temperature -40.0 °C		0.599 ft-lb/in
@Temperature -40.0 °F		50%RH; ASTM D256
 0.430 J/cm
@Temperature -40.0 °C		0.806 ft-lb/in
@Temperature -40.0 °F		DAM; ASTM D256
 0.430 J/cm
@Temperature 23.0 °C		0.806 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 0.750 J/cm
@Temperature 23.0 °C		1.41 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 5.00 kJ/m²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 5.00 kJ/m²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 6.00 kJ/m²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Charpy Impact Unnotched  NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		DAM; ISO 179/1eU
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.400 J/cm²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.500 J/cm²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.700 J/cm²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		50%RH; ASTM D257
 1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+14 ohm-cm
@Temperature 23.0 °C		1.00e+14 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Surface Resistance  1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		DAM; IEC 60093
 1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		50%RH; ASTM D257
 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		DAM; ASTM D257
Dielectric Constant  3.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.4
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.4
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 3.6
@Frequency 100 Hz,
Temperature 23.0 °C		3.6
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 5.3
@Frequency 100 Hz,
Temperature 23.0 °C		5.3
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dielectric Strength  21.7 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		551 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		50%RH; IEC 60243-1
 22.6 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		574 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.014
@Frequency 100 Hz,
Temperature 23.0 °C		0.014
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.016
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.016
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 100 Hz,
Temperature 23.0 °C		0.020
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.040
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.040
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.10
@Frequency 100 Hz,
Temperature 23.0 °C		0.10
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Comparative Tracking Index  600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; IEC 60112
 >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  90.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		50.0 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 120 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 180 µm/m-°C
@Temperature 55.0 - 160 °C		100 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 218 °C424 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 135 °C275 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C131 °FDAM; ASTM D648
 62.0 °C144 °FDAM; ISO 75-1/-2
Brittleness Temperature -126 °C-195 °FDAM; ASTM D746
 -109 °C-164 °F50%RH; ASTM D746
UL RTI, Electrical  105 °C
@Thickness 3.00 mm		221 °F
@Thickness 0.118 in		DAM; UL 746B
 105 °C
@Thickness 1.50 mm		221 °F
@Thickness 0.0591 in		DAM; UL 746B
 105 °C
@Thickness 0.860 mm		221 °F
@Thickness 0.0339 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.860 mm		149 °F
@Thickness 0.0339 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.860 mm		149 °F
@Thickness 0.0339 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.860 mm		HB
@Thickness 0.0339 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.860 mm		HB
@Thickness 0.0339 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
Oxygen Index 27 %27 %DAM; ISO 4589-1/-2
Glow Wire Test  700 °C
@Thickness 0.860 mm		1290 °F
@Thickness 0.0339 in		DAM; Ignition; IEC 60695-2-13
 700 °C
@Thickness 3.00 mm		1290 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 700 °C
@Thickness 1.50 mm		1290 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 775 °C
@Thickness 1.50 mm		1430 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 825 °C
@Thickness 0.860 mm		1520 °F
@Thickness 0.0339 in		DAM; IEC 60695-2-12
 925 °C
@Thickness 3.00 mm		1700 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 218 °C424 °F10°C/min; DAM; ISO 11357-1/-3
 250 °C482 °FDAM; Optimum
 230 - 290 °C446 - 554 °FDAM
Mold Temperature 70.0 °C158 °FDAM; optimum
 50.0 - 90.0 °C122 - 194 °FDAM
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.15 %<= 0.15 %DAM
 
Descriptive Properties
AdditiveHeat StabilizerDAM
 LubricantDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
Extrudable - Blown FilmYesDAM
Extrudable - CoatingYesDAM
Extrudable - FilamentYesDAM
Extrudable - HoseYesDAM
Extrudable - SheetYesDAM
Extrudable - TubingYesDAM
Extrudable - Wire and CableYesDAM
Extrusion Blow MoldableYesDAM
FeaturesChemical Resistance, GoodDAM
 Electrical Properties, GoodDAM
 Heat Aging Resistance, GoodDAM
 LubricatedDAM
FormsPelletsDAM
GenericNylon 612DAM
Heat StabilizedYesDAM
Injection Blow MoldableYesDAM
Material StatusCurrentDAM
Part Marking Code>PA612<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA612DAM
Processing MethodExtrusionDAM
 ExtrusionDAM
 Injection MoldingDAM
Product CategoryExtrusion ResinsDAM
 Unreinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA612ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAutomotive ApplicationsDAM
 Cable JacketingDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47476.html

免责声明: 本文 DuPont Performance Polymers Zytel® 153HSL NC010 Nylon 612 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4