- 密度 [g/cm3]: 1.24
- 缺口冲击强度: 1.28
- 弯曲强度 [MPa]: 165.0
- 弯曲模量 [MPa]: 13.5
- 硬度: 106.0
- 热变形温度 [℃]: 209.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 165 MPa | 23900 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| Flexural Modulus | 13.5 GPa | 1960 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm | 2.40 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.26 J/cm | 13.6 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 195 - 215 °C | 383 - 419 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ASTM D648 |