- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.96
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.518
- 拉伸强度 [MPa]: 31.0
- 断裂伸长率 [%]: 4.48
- 弯曲强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 1.50
- 硬度: 80.0
- 热变形温度 [℃]: 127.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 - 1.44 g/cc | 0.0347 - 0.0520 lb/in³ | Average value: 1.12 g/cc Grade Count:37 |
| Filler Content | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 24.2 % Grade Count:18 |
| Water Absorption | 0.0100 - 0.0600 % | 0.0100 - 0.0600 % | Average value: 0.0264 % Grade Count:14 |
| Linear Mold Shrinkage | 0.00100 - 0.0226 cm/cm | 0.00100 - 0.0226 in/in | Average value: 0.00522 cm/cm Grade Count:33 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00400 - 0.00900 cm/cm | 0.00400 - 0.00900 in/in | Average value: 0.00538 cm/cm Grade Count:13 |
| Linear Mold Shrinkage, Transverse | 0.00930 - 0.0210 cm/cm | 0.00930 - 0.0210 in/in | Average value: 0.0140 cm/cm Grade Count:5 |
| Melt Flow | 0.900 - 16.0 g/10 min | 0.900 - 16.0 g/10 min | Average value: 7.14 g/10 min Grade Count:17 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 80.0 - 115 | 80.0 - 115 | Average value: 95.9 Grade Count:18 |
| Tensile Strength, Ultimate | 20.0 - 115 MPa | 2900 - 16700 psi | Average value: 53.0 MPa Grade Count:31 |
| Tensile Strength, Yield | 31.0 - 95.0 MPa | 4500 - 13800 psi | Average value: 64.4 MPa Grade Count:7 |
| Elongation at Break | 2.00 - 11.0 % | 2.00 - 11.0 % | Average value: 5.55 % Grade Count:30 |
| Elongation at Yield | 0.600 - 2.50 % | 0.600 - 2.50 % | Average value: 1.87 % Grade Count:3 |
| Modulus of Elasticity | 1.50 - 9.50 GPa | 218 - 1380 ksi | Average value: 4.46 GPa Grade Count:23 |
| Flexural Yield Strength | 4.48 - 145 MPa | 650 - 21000 psi | Average value: 75.9 MPa Grade Count:31 |
| Flexural Modulus | 1.50 - 7.85 GPa | 218 - 1140 ksi | Average value: 4.04 GPa Grade Count:36 |
| Izod Impact, Notched | 0.518 - 2.14 J/cm | 0.970 - 4.00 ft-lb/in | Average value: 1.24 J/cm Grade Count:30 |
| 1.30 - 1.30 J/cm @Temperature -40.0 - -40.0 °C | 2.44 - 2.44 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.30 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 2.14 - 10.7 J/cm | 4.00 - 20.0 ft-lb/in | Average value: 5.31 J/cm Grade Count:21 |
| 4.80 - 4.80 J/cm @Temperature -40.0 - -40.0 °C | 8.99 - 8.99 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 4.80 J/cm Grade Count:2 | |
| Izod Impact, Notched (ISO) | 6.50 - 16.0 kJ/m² | 3.09 - 7.61 ft-lb/in² | Average value: 11.0 kJ/m² Grade Count:4 |
| Charpy Impact Unnotched | 1.60 - 7.50 J/cm² | 7.61 - 35.7 ft-lb/in² | Average value: 4.16 J/cm² Grade Count:7 |
| 1.00 - 4.70 J/cm² @Temperature -20.0 - -20.0 °C | 4.76 - 22.4 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 2.98 J/cm² Grade Count:4 | |
| Charpy Impact, Notched | 0.200 - 1.00 J/cm² | 0.952 - 4.76 ft-lb/in² | Average value: 0.617 J/cm² Grade Count:6 |
| 0.100 - 0.800 J/cm² @Temperature -20.0 - -20.0 °C | 0.476 - 3.81 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 0.425 J/cm² Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+16 ohm-cm | 1.00e+14 - 1.00e+16 ohm-cm | Average value: 7.08e+15 ohm-cm Grade Count:16 |
| Surface Resistance | 1.00e+12 - 1.00e+14 ohm | 1.00e+12 - 1.00e+14 ohm | Average value: 6.70e+13 ohm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 145 - 168 °C | 293 - 334 °F | Average value: 161 °C Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 - 166 °C | 260 - 331 °F | Average value: 150 °C Grade Count:26 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 - 160 °C | 153 - 320 °F | Average value: 132 °C Grade Count:29 |
| Vicat Softening Point | 105 - 165 °C | 221 - 329 °F | Average value: 151 °C Grade Count:7 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:18 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 857 °C Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 246 °C | 380 - 475 °F | Average value: 215 °C Grade Count:18 |
| Melt Temperature | 170 - 250 °C | 338 - 482 °F | Average value: 218 °C Grade Count:5 |
| Mold Temperature | 32.2 - 80.0 °C | 90.0 - 176 °F | Average value: 52.3 °C Grade Count:19 |
| Injection Pressure | 68.9 - 120 MPa | 10000 - 17400 psi | Average value: 88.1 MPa Grade Count:18 |