- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.42
- 缺口冲击强度: 0.238
- 弯曲强度 [MPa]: 41.0
- 弯曲模量 [MPa]: 6.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.580 g/cc | 0.0210 lb/in³ | ASTM D1895 |
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.42 % | 0.42 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0074 cm/cm | 0.0074 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 81 | 81 | ASTM D785 |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Elongation at Break | 0.58 % | 0.58 % | ASTM D638 |
| Tensile Modulus | 7.70 GPa | 1120 ksi | ASTM D638 |
| Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ASTM D790 |
| Compressive Strength | 181 MPa | 26300 psi | ASTM D695 |
| Poissons Ratio | 0.34 | 0.34 | ASTM D638 |
| Shear Modulus | 2.87 GPa | 416 ksi | Calculated |
| Izod Impact, Notched | 0.238 J/cm | 0.446 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.254 J/cm² | 1.21 ft-lb/in² | ASTM D256 |
| Impact | 145 | 145 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.70e+11 ohm-cm | 4.70e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.4 | 5.4 | ASTM D150 |
| Dielectric Strength | 10.5 kV/mm | 267 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.058 | 0.058 | ASTM D150 |
| Arc Resistance | 128 sec | 128 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 188 °C | 370 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | |
| Oxygen Index | 27.5 % | 27.5 % | ASTM D2863 |
| Shrinkage | 0.35 % | 0.35 % | 72 hr, 120ºC; ASTM D1299 |