- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.26
- 断裂伸长率 [%]: 88.3
- 弯曲强度 [MPa]: 58.4
- 弯曲模量 [MPa]: 8.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.720 g/cc | 0.0260 lb/in³ | ASTM D1895 |
| Water Absorption | 0.26 % | 0.26 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0083 cm/cm | 0.0083 in/in | Post shrinkage is 0.31% at 72hr 120°C.; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 58.4 MPa | 8470 psi | ASTM D638 |
| Elongation at Break | 0.80 % | 0.80 % | ASTM D638 |
| Tensile Modulus | 8.60 GPa | 1250 ksi | ASTM D638 |
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 8.10 GPa | 1170 ksi | ASTM D790 |
| Compressive Yield Strength | 197.8 MPa | 28690 psi | ASTM D695 |
| Charpy Impact, Notched | 0.170 J/cm² | 0.809 ft-lb/in² | J/cm; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.34e+11 ohm-cm | 1.34e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.4 @Frequency 1e+6 Hz | 5.4 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 10.1 kV/mm | 257 kV/in | Short Term per ASTM D149. |
| Dissipation Factor | 0.067 @Frequency 1e+6 Hz | 0.067 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 140 sec | 140 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Resistance; ASTM D795 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 3.18 mm | V-1 @Thickness 0.125 in | |