- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.121
- 缺口冲击强度: 0.34
- 弯曲强度 [MPa]: 43.0
- 弯曲模量 [MPa]: 10.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.670 g/cc | 0.0242 lb/in³ | ASTM D1895 |
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| Water Absorption | 0.121 % | 0.121 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0049 cm/cm | 0.0049 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 81 | 81 | ASTM D785 |
| Tensile Strength, Ultimate | 43.0 MPa | 6240 psi | ASTM D638 |
| Elongation at Break | 0.51 % | 0.51 % | ASTM D638 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | ASTM D638 |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
| Compressive Strength | 156 MPa | 22600 psi | ASTM D695 |
| Poissons Ratio | 0.31 | 0.31 | ASTM D638 |
| Shear Modulus | 4.47 GPa | 648 ksi | Calculated |
| Izod Impact, Notched | 0.340 J/cm | 0.637 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.310 J/cm² | 1.48 ft-lb/in² | ASTM D256 |
| Impact | 188 | 188 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.60e+12 ohm-cm | 2.60e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.9 | 4.9 | ASTM D150 |
| Dielectric Strength | 13.6 kV/mm | 345 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.039 | 0.039 | ASTM D150 |
| Arc Resistance | 184 sec | 184 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 35.0 µm/m-°C @Temperature 40.0 - 130 °C | 19.4 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.580 W/m-K @Temperature 100 °C | 4.03 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 189 °C | 372 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 261 °C | 502 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 46 % | 46 % | ASTM D2863 |
| Shrinkage | 0.103 % | 0.103 % | 72 hr, 120ºC; ASTM D1299 |