- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.26
- 断裂伸长率 [%]: 88.1
- 弯曲强度 [MPa]: 56.8
- 弯曲模量 [MPa]: 8.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.740 g/cc | 0.0267 lb/in³ | ASTM D1895 |
| Water Absorption | 0.26 % | 0.26 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0081 cm/cm | 0.0081 in/in | Post shrinkage is 0.27% at 72hr 120°C.; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 56.8 MPa | 8240 psi | ASTM D638 |
| Elongation at Break | 0.90 % | 0.90 % | ASTM D638 |
| Tensile Modulus | 9.20 GPa | 1330 ksi | ASTM D638 |
| Flexural Yield Strength | 88.1 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ASTM D790 |
| Compressive Yield Strength | 189.9 MPa | 27540 psi | ASTM D695 |
| Charpy Impact, Notched | 0.170 J/cm² | 0.809 ft-lb/in² | J/cm; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.15e+11 ohm-cm | 1.15e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.2 @Frequency 1e+6 Hz | 5.2 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 7.40 kV/mm | 188 kV/in | Step-by-Step; ASTM D149 |
| 10.5 kV/mm | 267 kV/in | Short Term per ASTM D149 | |
| Dissipation Factor | 0.067 @Frequency 1e+6 Hz | 0.067 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 150 sec | 150 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 199 °C | 390 °F | Heat Resistance; ASTM D795 |
| Deflection Temperature at 1.8 MPa (264 psi) | 176 °C | 349 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.47 mm | V-1 @Thickness 0.0579 in | |