- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.09
- 缺口冲击强度: 0.57
- 弯曲强度 [MPa]: 57.0
- 弯曲模量 [MPa]: 12.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.710 g/cc | 0.0257 lb/in³ | ASTM D1895 |
| Density | 1.78 g/cc | 0.0643 lb/in³ | ASTM D792 |
| Water Absorption | 0.090 % | 0.090 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00143 cm/cm | 0.00143 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 78 | 78 | ASTM D785 |
| Tensile Strength, Ultimate | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 0.60 % | 0.60 % | ASTM D638 |
| Tensile Modulus | 13.1 GPa | 1900 ksi | ASTM D638 |
| Flexural Strength | 102 MPa | 14800 psi | ASTM D790 |
| Flexural Modulus | 12.8 GPa | 1860 ksi | ASTM D790 |
| Compressive Strength | 168 MPa | 24400 psi | ASTM D695 |
| Izod Impact, Notched | 0.570 J/cm | 1.07 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.620 J/cm² | 2.95 ft-lb/in² | ASTM D256 |
| Impact | 227 | 227 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.30e+12 ohm-cm | 1.30e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.0 | 5.0 | ASTM D150 |
| Dielectric Strength | 14.3 kV/mm | 363 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.033 | 0.033 | ASTM D150 |
| Arc Resistance | 184 sec | 184 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 42.0 µm/m-°C @Temperature 40.0 - 130 °C | 23.3 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 225 °C | 437 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 46 % | 46 % | ASTM D2863 |
| Shrinkage | 0.070 % | 0.070 % | 72 hr, 120ºC; ASTM D1299 |