- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.32
- 断裂伸长率 [%]: 79.7
- 弯曲强度 [MPa]: 57.4
- 弯曲模量 [MPa]: 7.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.670 g/cc | 0.0242 lb/in³ | ASTM D1895 |
| Water Absorption | 0.32 % | 0.32 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0107 cm/cm | 0.0107 in/in | Post shrinkage is 0.32% at 72hr 120°C.; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 84 | 84 | ASTM D785 |
| Tensile Strength, Ultimate | 57.4 MPa | 8330 psi | ASTM D638 |
| Elongation at Break | 0.80 % | 0.80 % | ASTM D638 |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ASTM D638 |
| Flexural Yield Strength | 79.7 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D790 |
| Compressive Yield Strength | 198.3 MPa | 28760 psi | ASTM D695 |
| Charpy Impact, Notched | 0.190 J/cm² | 0.904 ft-lb/in² | J/cm; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 4.36e+11 ohm-cm | 4.36e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.5 @Frequency 1e+6 Hz | 5.5 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 9.10 kV/mm | 231 kV/in | Step-by-Step; ASTM D149 |
| 10.6 kV/mm | 269 kV/in | Short Term per ASTM D149 | |
| Dissipation Factor | 0.062 @Frequency 1e+6 Hz | 0.062 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 140 sec | 140 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Resistance; ASTM D795 |
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C | 318 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 6.10 mm | V-1 @Thickness 0.240 in | |