- 密度 [g/cm3]: 1.83
- 吸水率 [%]: 0.056
- 缺口冲击强度: 0.33
- 弯曲强度 [MPa]: 76.0
- 弯曲模量 [MPa]: 15.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.830 g/cc | 0.0300 lb/in³ | ASTM D1895 |
| Density | 1.83 g/cc | 0.0661 lb/in³ | ASTM D792 |
| Water Absorption | 0.056 % | 0.056 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00094 cm/cm | 0.00094 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 95 | 95 | ASTM D785 |
| Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 0.67 % | 0.67 % | ASTM D638 |
| Tensile Modulus | 15.9 GPa | 2310 ksi | ASTM D638 |
| Flexural Strength | 139 MPa | 20200 psi | ASTM D790 |
| Flexural Modulus | 15.9 GPa | 2310 ksi | ASTM D790 |
| Compressive Strength | 226 MPa | 32800 psi | ASTM D695 |
| Izod Impact, Notched | 0.330 J/cm | 0.618 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.310 J/cm² | 1.48 ft-lb/in² | ASTM D256 |
| Impact | 203 | 203 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.10e+11 ohm-cm | 5.10e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.7 | 6.7 | ASTM D150 |
| Dielectric Strength | 8.10 kV/mm | 206 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.042 | 0.042 | ASTM D150 |
| Arc Resistance | 153 sec | 153 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.540 W/m-K @Temperature 100 °C | 3.75 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 217 °C | 423 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |
| Oxygen Index | 39 % | 39 % | ASTM D2863 |
| Shrinkage | 0.049 % | 0.049 % | 72 hr, 120ºC; ASTM D1299 |