- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.35
- 缺口冲击强度: 0.2
- 断裂伸长率 [%]: 81.8
- 弯曲强度 [MPa]: 53.3
- 弯曲模量 [MPa]: 7.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ASTM D1895 |
| Water Absorption | 0.35 % | 0.35 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0066 cm/cm | 0.0066 in/in | Post shrinkage is 0.25% at 72hr 120°C.; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 53.3 MPa | 7730 psi | ASTM D638 |
| Elongation at Break | 0.70 % | 0.70 % | ASTM D638 |
| Tensile Modulus | 8.60 GPa | 1250 ksi | ASTM D638 |
| Flexural Yield Strength | 81.8 MPa | 11900 psi | ASTM D790 |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ASTM D790 |
| Compressive Yield Strength | 217.9 MPa | 31600 psi | ASTM D695 |
| Izod Impact, Notched | 0.200 J/cm | 0.375 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | J/cm; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.0725e+11 ohm-cm | 3.0725e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.9 @Frequency 1e+6 Hz | 4.9 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 11.5 kV/mm | 292 kV/in | Short Term per ASTM D149. |
| Dissipation Factor | 0.049 @Frequency 1e+6 Hz | 0.049 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 140 sec | 140 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 193 °C | 379 °F | Heat Resistance; ASTM D795 |
| Deflection Temperature at 1.8 MPa (264 psi) | 183 °C | 361 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.10 mm | V-0 @Thickness 0.240 in | |