- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.925
- 拉伸强度 [MPa]: 14.5
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 50 | 50 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 7.45 MPa | 1080 psi | |||
| Tensile Strength, Yield | 14.5 MPa | 2100 psi | 2% Offset; ASTM D638 | ||
| Elongation at Break | 57 % | 57 % | ASTM D638 | ||
| 1% Secant Modulus | 430 MPa | 62400 psi | ASTM D790 | ||
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 122 °C | 252 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Brittleness Temperature | -76.1 °C | -105 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||