- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.6
- 缺口冲击强度: 0.694
- 拉伸强度 [MPa]: 60.0
- 断裂伸长率 [%]: 59.0
- 弯曲强度 [MPa]: 36.0
- 弯曲模量 [MPa]: 1.80
- 热变形温度 [℃]: 166.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 - 1.55 g/cc | 0.0401 - 0.0560 lb/in³ | Average value: 1.35 g/cc Grade Count:10 |
| Water Absorption | 0.600 - 3.10 % | 0.600 - 3.10 % | Average value: 1.50 % Grade Count:4 |
| Moisture Absorption at Equilibrium | 1.20 - 1.60 % | 1.20 - 1.60 % | Average value: 1.47 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 - 0.0120 cm/cm | 0.00200 - 0.0120 in/in | Average value: 0.00810 cm/cm Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 36.0 - 140 MPa | 5220 - 20300 psi | Average value: 80.4 MPa Grade Count:7 |
| Tensile Strength, Yield | 60.0 - 76.0 MPa | 8700 - 11000 psi | Average value: 72.4 MPa Grade Count:3 |
| Elongation at Break | 2.00 - 23.0 % | 2.00 - 23.0 % | Average value: 14.9 % Grade Count:7 |
| Modulus of Elasticity | 2.60 - 10.0 GPa | 377 - 1450 ksi | Average value: 6.11 GPa Grade Count:5 |
| Flexural Yield Strength | 59.0 - 205 MPa | 8560 - 29700 psi | Average value: 116 MPa Grade Count:10 |
| Flexural Modulus | 1.80 - 9.00 GPa | 261 - 1310 ksi | Average value: 5.06 GPa Grade Count:9 |
| Izod Impact, Notched | 0.694 - 1.49 J/cm | 1.30 - 2.79 ft-lb/in | Average value: 1.08 J/cm Grade Count:3 |
| Izod Impact, Unnotched | 6.41 J/cm - NB | 12.0 ft-lb/in - NB | Average value: 6.41 J/cm Grade Count:3 |
| Charpy Impact Unnotched | 2.00 - 5.40 J/cm² | 9.52 - 25.7 ft-lb/in² | Average value: 3.60 J/cm² Grade Count:5 |
| 1.50 - 1.50 J/cm² @Temperature -20.0 - -20.0 °C | 7.14 - 7.14 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 1.50 J/cm² Grade Count:1 | |
| Charpy Impact, Notched | 0.500 - 0.700 J/cm² | 2.38 - 3.33 ft-lb/in² | Average value: 0.600 J/cm² Grade Count:5 |
| 0.390 - 0.500 J/cm² @Temperature -30.0 - -20.0 °C | 1.86 - 2.38 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 0.430 J/cm² Grade Count:3 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+17 ohm-cm | 1.00e+15 - 1.00e+17 ohm-cm | Average value: 2.57e+16 ohm-cm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 205 - 225 °C | 401 - 437 °F | Average value: 218 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 - 191 °C | 331 - 376 °F | Average value: 176 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 - 200 °C | 136 - 392 °F | Average value: 114 °C Grade Count:9 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 275 °C | 430 - 527 °F | Average value: 261 °C Grade Count:7 |
| Nozzle Temperature | 235 - 280 °C | 455 - 536 °F | Average value: 263 °C Grade Count:3 |
| Melt Temperature | 200 - 300 °C | 392 - 572 °F | Average value: 260 °C Grade Count:4 |
| Mold Temperature | 50.0 - 110 °C | 122 - 230 °F | Average value: 79.1 °C Grade Count:7 |
| Drying Temperature | 75.0 - 130 °C | 167 - 266 °F | Average value: 92.5 °C Grade Count:6 |
| Dry Time | 2.00 - 5.00 hour | 2.00 - 5.00 hour | Average value: 4.00 hour Grade Count:3 |
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | Average value: 86.5 MPa Grade Count:4 |