- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.427
- 拉伸强度 [MPa]: 86.2
- 断裂伸长率 [%]: 65.0
- 弯曲强度 [MPa]: 1.28
- 弯曲模量 [MPa]: 0.0873
- 硬度: 109.0
- 热变形温度 [℃]: 204.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 - 1.75 g/cc | 0.0462 - 0.0632 lb/in³ | Average value: 1.43 g/cc Grade Count:202 |
| Filler Content | 35.0 - 45.0 % | 35.0 - 45.0 % | Average value: 39.7 % Grade Count:37 |
| Water Absorption | 0.200 - 7.10 % | 0.200 - 7.10 % | Average value: 3.05 % Grade Count:119 |
| Moisture Absorption at Equilibrium | 0.250 - 6.20 % | 0.250 - 6.20 % | Average value: 1.94 % Grade Count:63 |
| Water Absorption at Saturation | 4.80 - 7.50 % | 4.80 - 7.50 % | Average value: 5.90 % Grade Count:21 |
| Additive Loading | 40.0 % | 40.0 % | Average value: 40.0 % Grade Count:3 |
| Viscosity | 2.60 - 50.0 cP | 2.60 - 50.0 cP | Average value: 18.4 cP Grade Count:3 |
| Viscosity Measurement | 0.740 - 160 | 0.740 - 160 | Average value: 124 Grade Count:26 |
| Viscosity Test | 140 - 150 cm³/g | 140 - 150 cm³/g | Average value: 144 cm³/g Grade Count:5 |
| Maximum Moisture Content | 0.100 | 0.100 | Average value: 0.100 Grade Count:4 |
| Linear Mold Shrinkage | 0.000300 - 0.0350 cm/cm | 0.000300 - 0.0350 in/in | Average value: 0.00413 cm/cm Grade Count:153 |
| 0.00300 - 0.00300 cm/cm @Temperature 80.0 - 80.0 °C | 0.00300 - 0.00300 in/in @Temperature 176 - 176 °F | Average value: 0.00300 cm/cm Grade Count:2 | |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.00400 cm/cm | 0.00300 - 0.00400 in/in | Average value: 0.00320 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, Transverse | 0.000700 - 0.0590 cm/cm | 0.000700 - 0.0590 in/in | Average value: 0.00763 cm/cm Grade Count:55 |
| 0.00600 - 0.00700 cm/cm @Temperature 80.0 - 80.0 °C | 0.00600 - 0.00700 in/in @Temperature 176 - 176 °F | Average value: 0.00650 cm/cm Grade Count:2 | |
| Melt Flow | 1.00 - 78.7 g/10 min | 1.00 - 78.7 g/10 min | Average value: 33.7 g/10 min Grade Count:21 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 88.0 - 100 | 88.0 - 100 | Average value: 92.3 Grade Count:8 |
| Hardness, Rockwell R | 109 - 124 | 109 - 124 | Average value: 121 Grade Count:41 |
| Hardness, Shore D | 77.0 - 91.0 | 77.0 - 91.0 | Average value: 82.5 Grade Count:5 |
| Ball Indentation Hardness | 84.0 - 245 MPa | 12200 - 35500 psi | Average value: 162 MPa Grade Count:16 |
| Tensile Strength, Ultimate | 1.28 - 237 MPa | 186 - 34400 psi | Average value: 149 MPa Grade Count:154 |
| 77.0 - 281.306 MPa @Temperature -40.0 - 121 °C | 11200 - 40800.1 psi @Temperature -40.0 - 250 °F | Average value: 72.2 MPa Grade Count:3 | |
| 60.0 - 102.5 MPa @Temperature 130 - 175 °C | 8700 - 14870 psi @Temperature 266 - 347 °F | Average value: 72.2 MPa Grade Count:4 | |
| 60.0 - 102.5 MPa @Time 1.80e+7 - 7.20e+7 sec | 8700 - 14870 psi @Time 5000 - 20000 hour | Average value: 72.2 MPa Grade Count:4 | |
| 0.510 - 268.29 MPa @Strain 0.000 - 12.2 % | 74.0 - 38912 psi @Strain 0.000 - 12.2 % | Average value: 72.2 MPa Grade Count:2 | |
| 0.510 - 268.29 MPa @Temperature -20.0 - 200 °C | 74.0 - 38912 psi @Temperature -4.00 - 392 °F | Average value: 72.2 MPa Grade Count:2 | |
| Tensile Strength, Yield | 86.2 - 234 MPa | 12500 - 34000 psi | Average value: 176 MPa Grade Count:52 |
| Elongation at Break | 1.00 - 25.0 % | 1.00 - 25.0 % | Average value: 3.73 % Grade Count:171 |
| 2.60 - 7.00 % @Temperature -40.0 - 121 °C | 2.60 - 7.00 % @Temperature -40.0 - 250 °F | Average value: 5.10 % Grade Count:2 | |
| Elongation at Yield | 2.00 - 22.0 % | 2.00 - 22.0 % | Average value: 4.46 % Grade Count:26 |
| Modulus of Elasticity | 1.31 - 15.9 GPa | 190 - 2300 ksi | Average value: 9.79 GPa Grade Count:134 |
| 5.00 - 12.0 GPa @Temperature -40.0 - 140 °C | 725 - 1740 ksi @Temperature -40.0 - 284 °F | Average value: 9.52 GPa Grade Count:2 | |
| Flexural Yield Strength | 65.0 - 352 MPa | 9430 - 51100 psi | Average value: 247 MPa Grade Count:138 |
| 138 - 450 MPa @Temperature -40.0 - 121 °C | 20000 - 65300 psi @Temperature -40.0 - 250 °F | Average value: 249 MPa Grade Count:5 | |
| Flexural Modulus | 0.0873 - 13.8 GPa | 12.7 - 2000 ksi | Average value: 9.23 GPa Grade Count:152 |
| 4.83 - 12.4795 GPa @Temperature -40.0 - 121 °C | 701 - 1810.03 ksi @Temperature -40.0 - 250 °F | Average value: 6.81 GPa Grade Count:5 | |
| Compressive Yield Strength | 149 - 258 MPa | 21600 - 37400 psi | Average value: 184 MPa Grade Count:12 |
| Poissons Ratio | 0.350 | 0.350 | Average value: 0.350 Grade Count:3 |
| Shear Modulus | 4.60 - 5.00 GPa | 667 - 725 ksi | Average value: 4.73 GPa Grade Count:3 |
| Izod Impact, Notched | 0.427 - 3.68 J/cm | 0.800 - 6.90 ft-lb/in | Average value: 1.50 J/cm Grade Count:84 |
| 1.91 - 5.12544 J/cm @Temperature -40.0 - 121 °C | 3.58 - 9.60205 ft-lb/in @Temperature -40.0 - 250 °F | Average value: 1.85 J/cm Grade Count:3 | |
| 0.74746 - 1.28136 J/cm @Temperature -40.0 - -40.0 °C | 1.4003 - 2.40051 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.85 J/cm Grade Count:3 | |
| 0.74746 - 1.28136 J/cm @Thickness 3.17 - 3.17 mm | 1.4003 - 2.40051 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.85 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 3.20 - 14.4 J/cm | 6.00 - 27.0 ft-lb/in | Average value: 11.1 J/cm Grade Count:38 |
| Izod Impact, Notched (ISO) | 5.50 - 79.0 kJ/m² | 2.62 - 37.6 ft-lb/in² | Average value: 18.8 kJ/m² Grade Count:53 |
| 10.0 - 27.0 kJ/m² @Temperature -40.0 - -30.0 °C | 4.76 - 12.8 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 14.1 kJ/m² Grade Count:16 | |
| Izod Impact, Unnotched (ISO) | 70.0 - 150 kJ/m² | 33.3 - 71.4 ft-lb/in² | Average value: 82.6 kJ/m² Grade Count:16 |
| 60.0 - 90.0 kJ/m² @Temperature -30.0 - -30.0 °C | 28.6 - 42.8 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 74.2 kJ/m² Grade Count:5 | |
| Charpy Impact Unnotched | 3.50 J/cm² - NB | 16.7 ft-lb/in² - NB | Average value: 8.94 J/cm² Grade Count:98 |
| 3.30 J/cm² - NB @Temperature -40.0 - 30.0 °C | 15.7 ft-lb/in² - NB @Temperature -40.0 - 86.0 °F | Average value: 7.57 J/cm² Grade Count:62 | |
| Charpy Impact, Notched | 0.380 - 11.7 J/cm² | 1.81 - 55.4 ft-lb/in² | Average value: 2.03 J/cm² Grade Count:104 |
| 0.370 - 1.90 J/cm² @Temperature -40.0 - 30.0 °C | 1.76 - 9.04 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 1.23 J/cm² Grade Count:51 | |
| Puncture Energy | 2.30 - 13.0 J | 1.70 - 9.59 ft-lb | Average value: 7.05 J Grade Count:3 |
| 1.60 - 7.00 J @Temperature -30.0 - -30.0 °C | 1.18 - 5.16 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 3.97 J Grade Count:3 | |
| Tensile Creep Modulus, 1000 hours | 3300 - 8700 MPa | 479000 - 1.26e+6 psi | Average value: 5540 MPa Grade Count:9 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+8 - 1.40e+16 ohm-cm | 1.00e+8 - 1.40e+16 ohm-cm | Average value: 5.64e+14 ohm-cm Grade Count:100 |
| 1.00e+8 - 1.00e+16 ohm-cm @Temperature 40.0 - 140 °C | 1.00e+8 - 1.00e+16 ohm-cm @Temperature 104 - 284 °F | Average value: 1.46e+15 ohm-cm Grade Count:2 | |
| Surface Resistance | 1.00e+10 - 1.00e+16 ohm | 1.00e+10 - 1.00e+16 ohm | Average value: 2.83e+14 ohm Grade Count:49 |
| Dielectric Constant | 3.30 - 20.0 | 3.30 - 20.0 | Average value: 5.57 Grade Count:46 |
| Dielectric Strength | 11.0 - 80.0 kV/mm | 280 - 2030 kV/in | Average value: 29.4 kV/mm Grade Count:61 |
| Dissipation Factor | 0.00500 - 0.300 | 0.00500 - 0.300 | Average value: 0.0783 Grade Count:49 |
| Arc Resistance | 120 - 130 sec | 120 - 130 sec | Average value: 123 sec Grade Count:3 |
| Comparative Tracking Index | 350 - 600 V | 350 - 600 V | Average value: 529 V Grade Count:70 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.100 - 500 µm/m-°C | 0.0556 - 278 µin/in-°F | Average value: 28.3 µm/m-°C Grade Count:62 |
| CTE, linear, Transverse to Flow | 0.150 - 100 µm/m-°C | 0.0833 - 55.6 µin/in-°F | Average value: 52.6 µm/m-°C Grade Count:32 |
| Specific Heat Capacity | 1.30 - 2.52 J/g-°C | 0.311 - 0.603 BTU/lb-°F | Average value: 1.63 J/g-°C Grade Count:9 |
| Thermal Conductivity | 0.280 - 0.490 W/m-K | 1.94 - 3.40 BTU-in/hr-ft²-°F | Average value: 0.345 W/m-K Grade Count:21 |
| Melting Point | 215 - 295 °C | 419 - 563 °F | Average value: 225 °C Grade Count:118 |
| Maximum Service Temperature, Air | 90.0 - 270 °C | 194 - 518 °F | Average value: 162 °C Grade Count:36 |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 242 °C | 400 - 468 °F | Average value: 218 °C Grade Count:92 |
| Deflection Temperature at 1.8 MPa (264 psi) | 2.60 - 270 °C | 36.7 - 518 °F | Average value: 208 °C Grade Count:155 |
| Deflection Temperature at 8.0 MPa | 120 - 170 °C | 248 - 338 °F | Average value: 152 °C Grade Count:13 |
| Vicat Softening Point | 200 - 222 °C | 392 - 432 °F | Average value: 208 °C Grade Count:23 |
| Decomposition Temperature | 300 - 350 °C | 572 - 662 °F | Average value: 325 °C Grade Count:12 |
| UL RTI, Electrical | 65.0 - 140 °C | 149 - 284 °F | Average value: 135 °C Grade Count:11 |
| UL RTI, Mechanical with Impact | 65.0 - 125 °C | 149 - 257 °F | Average value: 117 °C Grade Count:11 |
| UL RTI, Mechanical without Impact | 65.0 - 150 °C | 149 - 302 °F | Average value: 140 °C Grade Count:11 |
| Flammability, UL94 | HB - 5VB | HB - 5VB | Grade Count:96 |
| Oxygen Index | 23.0 - 27.0 % | 23.0 - 27.0 % | Average value: 23.7 % Grade Count:7 |
| Glow Wire Test | 550 - 750 °C | 1020 - 1380 °F | Average value: 650 °C Grade Count:23 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 288 °C | 158 - 550 °F | Average value: 167 °C Grade Count:27 |
| Feed Temperature | 20.0 - 260 °C | 68.0 - 500 °F | Average value: 159 °C Grade Count:10 |
| Nozzle Temperature | 230 - 293 °C | 446 - 560 °F | Average value: 262 °C Grade Count:9 |
| Melt Temperature | 80.0 - 370 °C | 176 - 698 °F | Average value: 274 °C Grade Count:78 |
| Mold Temperature | 37.8 - 121 °C | 100 - 250 °F | Average value: 86.8 °C Grade Count:83 |
| Drying Temperature | 70.0 - 110 °C | 158 - 230 °F | Average value: 83.7 °C Grade Count:68 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 4.30 hour Grade Count:46 |
| 2.00 - 6.00 hour @Temperature 79.4 - 80.0 °C | 2.00 - 6.00 hour @Temperature 175 - 176 °F | Average value: 3.50 hour Grade Count:4 | |
| Moisture Content | 0.0300 - 0.200 % | 0.0300 - 0.200 % | Average value: 0.146 % Grade Count:49 |
| Dew Point | -30.0 - -17.8 °C | -22.0 - 0.000 °F | Average value: -21.0 °C Grade Count:11 |
| Injection Pressure | 4.96 - 138 MPa | 720 - 20000 psi | Average value: 80.9 MPa Grade Count:29 |
| Back Pressure | 0.000 - 1.72 MPa | 0.000 - 250 psi | Average value: 0.573 MPa Grade Count:5 |
| Screw Speed | 20.0 - 100 rpm | 20.0 - 100 rpm | Average value: 57.5 rpm Grade Count:3 |